| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 | ||
| Melt Flow | 25 g/10 min @Load 10.0 kg, Temperature 220 °C |
25 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 78.0 MPa | 11300 psi | H358/30; ISO 2039-1 | ||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | 50 mm/min; ISO 527 | ||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 | ||
| Elongation at Break | 10 % | 10 % | 50 mm/min; ISO 527 | ||
| Flexural Strength | 57.0 MPa | 8270 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C | ||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | unannealed; ISO 75 | ||
| 97.0 °C | 207 °F | annealed; ISO 75 | |||
| Vicat Softening Point | 85.0 °C @Load 5.00 kg |
185 °F @Load 11.0 lb |
50°C/hr; ISO 306 | ||
| 88.0 °C @Load 5.00 kg |
190 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |||
| 99.0 °C @Load 1.00 kg |
210 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |||
| 99.0 °C @Load 1.00 kg |
210 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |||
| Flammability, UL94 | V-0 @Thickness 2.54 mm |
V-0 @Thickness 0.100 in |
UL 94 | ||
| 5VA @Thickness 3.17 mm |
5VA @Thickness 0.125 in |
UL 94 | |||
| De |
|||||
| Impact Flexural Test Notched (KJ/m²) | 11 | ||||
| Impact Flexural Test Unnotched (KJ/m²) | 110 | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com