| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 | ||
| Water Absorption | 2.7 % | 2.7 % | ISO 62 | ||
| Moisture Absorption | 1.20 % | 1.20 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.030 cm/cm | 0.030 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 70.0 MPa | 10200 psi | conditioned; ISO 2039-1 | ||
| 100 MPa | 14500 psi | dry; ISO 2039-1 | |||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 | ||
| 50.0 MPa | 7250 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | >= 50 % | >= 50 % | dry; ISO 527-1/-2 | ||
| >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |||
| Elongation at Yield | 5.0 % | 5.0 % | dry; ISO 527-1/-2 | ||
| 20 % | 20 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 1.20 GPa | 174 ksi | conditioned; ISO 527-1/-2 | ||
| 2.00 GPa | 290 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU | ||
| NB | NB | conditioned; ISO 179/1eU | |||
| NB @Temperature 30.0 °C |
NB @Temperature 86.0 °F |
dry; ISO 179/1eU | |||
| NB @Temperature 30.0 °C |
NB @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 4.00 J/cm² | 19.0 ft-lb/in² | dry; ISO 179/1eA | ||
| 9.00 J/cm² | 42.8 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 1.20 J/cm² @Temperature 30.0 °C |
5.71 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |||
| 1.30 J/cm² @Temperature 30.0 °C |
6.19 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | dry; IEC 60093 | ||
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 | |||
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 | ||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | dry; IEC 60243-1 | ||
| 40.0 kV/mm | 1020 kV/in | conditioned; IEC 60243-1 | |||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 160 µm/m-°C | 88.9 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 210 °C | 410 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 120 - 140 °C | 248 - 284 °F | long term; EMS | ||
| 160 °C | 320 °F | short term; EMS | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| De |
|||||
| Automotive | Air intake sytems | ||||
| Automotive electr. and electronics, lighting | |||||
| Compressed air systems | |||||
| Cooling and climate control | |||||
| Hydraulic systems | |||||
| Electricals & Electronics | Cables & Tubes | ||||
| Form | Granules | ||||
| Industry & Consumer goods | Hydraulics & Pneumatics | ||||
| Processing | Other Extrusion | ||||
| Profile Extrusion | |||||
| Product Attributes | High viscosity | ||||
| Hydrolysis resistant | |||||
| Special Characteristics | High impact or impact modified | ||||
| Improved heat resistance | |||||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。
上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！
可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：
联系人：邓小姐
联系电话：13917657923
联系QQ:996152797
联系邮箱：996152797@qq.com