类别：聚合物；热塑性；尼龙；尼龙66；尼龙66，无筋
材料说明：说明：Ultramid A3K Q601是一种易于流动，注塑级尼龙66。
应用范围：典型的应用包括快速处理高应力技术部件或电气绝缘部件。
物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 2.8 % | 2.8 % | 50% RH; ISO 62 | ||
| 8.5 % | 8.5 % | Saturation; ISO 62 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 | ||
| Elongation at Break | 20 % | 20 % | Nominal; ISO 527 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 | ||
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 | ||
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 | ||
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO 180 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179 | ||
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 | |||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | >= 0.20 % | >= 0.20 % | |||
| Injection Pressure | 35.0 - 125 MPa | 5080 - 18100 psi | |||
| De |
|||||
| Commercial Status | North America | ||||