| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 | ||
| Water Absorption | 9.0 % | 9.0 % | ISO 62 | ||
| Moisture Absorption | 3.00 % | 3.00 % | ISO 62 | ||
| Water Vapor Transmission | 15.0 g/m²/day | 0.966 g/100 in²/day | 23°C/85%r.h.; DIS 15106-1/-2 | ||
| Oxygen Transmission Rate | 25.0 cc/m²/day | 1.61 cc/100 in²/day | 23°C/0%r.h.; DIS 15105-1/-2 | ||
| 50.0 cc/m²/day | 3.22 cc/100 in²/day | 23°C/85%r.h.; DIS 15105-1/-2 | |||
| Carbon Dioxide Transmission | 80.0 cc-mm/m²-24hr-atm | 203 cc-mil/100 in²-24hr-atm | 23°C/0%r.h.; DIS 15105-1/-2 | ||
| 250 cc-mm/m²-24hr-atm | 635 cc-mil/100 in²-24hr-atm | 23°C/85%r.h.; DIS 15105-1/-2 | |||
| Melt Flow | 15 g/10 min | 15 g/10 min | (MVR) [cm³/10min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 35.0 MPa | 5080 psi | ISO 527-3 | ||
| Film Tensile Strength at Yield, TD | 30.0 MPa | 4350 psi | ISO 527-3 | ||
| Film Elongation at Break, MD | 700 % | 700 % | ISO 527-3 | ||
| Film Elongation at Break, TD | 700 % | 700 % | ISO 527-3 | ||
| Film Elongation at Yield, MD | 15 % | 15 % | ISO 527-3 | ||
| Film Elongation at Yield, TD | 15 % | 15 % | ISO 527-3 | ||
| Tensile Modulus | 0.750 GPa | 109 ksi | conditioned; ISO 527-1/-2 | ||
| 3.00 GPa | 435 ksi | dry; ISO 527-1/-2 | |||
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | ISO 8295 | ||
| Tear Strength | 30.0 kN/m | 171 pli | Trouser Tear resistance MD; ISO 6383-1 | ||
| 30.0 kN/m | 171 pli | Trouser Tear resistance TD; ISO 6383-1 | |||
| Elmendorf Tear Strength MD | 1020 g | 1020 g | ISO 6383-2 | ||
| Elmendorf Tear Strength TD | 1020 g | 1020 g | ISO 6383-2 | ||
| Film Tensile Strength at Break, MD | 100 MPa | 14500 psi | ISO 527-3 | ||
| Film Tensile Strength at Break, TD | 90.0 MPa | 13100 psi | ISO 527-3 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 | ||
| Optical Properties | Metric | English | Comments | ||
| Gloss | 100 % | 100 % | 60°; ISO 2813 | ||
| De |
|||||
| Food contact | EU Requirements | ||||
| FDA | |||||
| Form | Granules | ||||
| Gelboflextest [holes/m²], EMS | 900 | ||||
| Industry & Consumer goods | Mechanical Engineering | ||||
| Packaging | Blow moulded containers | ||||
| Non oriented film | |||||
| Oriented film | |||||
| Tubes | |||||
| Processing | Blown Film Extrusion | ||||
| Extrusion - blow molding | |||||
| Film Extrusion | |||||
| Other Extrusion | |||||
| Product Attributes | Barrier Properties | ||||
| High viscosity | |||||
| Nucleated | |||||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。