类别：聚合物；热塑性；聚苯醚/ PPO；聚苯乙烯（PS）；聚苯乙烯+聚苯醚，无筋
材料说明：典型的应用：光伏产业零部件
UL94 V-0阻燃
PTS PPE-LXS112的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Temperature 23.0 °C, Time 86400 sec |
0.10 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 40 g/10 min @Load 5.00 kg, Temperature 300 °C |
40 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | type I; ASTM D638 |
| Elongation at Break | 25 % | 25 % | type I; ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | 2.6 mm/min; ASTM D790 |
| Flexural Modulus | 2.35 GPa | 341 ksi | 2.6 mm/min; ASTM D790 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C @Thickness 6.40 mm |
248 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
||