| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Melt Flow | 27 g/10 min | 27 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | |
| Elongation at Break | 45 % | 45 % | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| Modulus of Elasticity | 2.10 GPa | 305 ksi | |
| Charpy Impact Unnotched | 15.0 J/cm² | 71.4 ft-lb/in² | |
| Charpy Impact, Notched | 2.50 J/cm² | 11.9 ft-lb/in² | |
| Tensile Impact Strength | 110 kJ/m² | 52.3 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 1700 MPa | 247000 psi | |
| Tensile Creep Modulus, 1000 hours | 1200 MPa | 174000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 4.00e+14 ohm | 4.00e+14 ohm | |
| Dielectric Constant | 2.0 @Frequency 100 Hz |
2.0 @Frequency 100 Hz |
|
| 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 38.0 kV/mm | 965 kV/in | |
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
|
| 0.0011 @Frequency 1e+6 Hz |
0.0011 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 300 V | 300 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | |
| Vicat Softening Point | 132 °C | 270 °F | 50°C/hr/50 N |