| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | |
| Water Absorption | 0.00 % | 0.00 % | |
| Melt Flow | 96 g/10 min | 96 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| Charpy Impact, Notched | 3.30 J/cm² | 15.7 ft-lb/in² | |
| Tensile Impact Strength | 268 kJ/m² | 128 ft-lb/in² | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 3.00e+14 ohm | 3.00e+14 ohm | |
| Dielectric Constant | 2.0 @Frequency 100 Hz |
2.0 @Frequency 100 Hz |
|
| 2.0 @Frequency 1e+6 Hz |
2.0 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | |
| Dissipation Factor | 0.00010 @Frequency 100 Hz |
0.00010 @Frequency 100 Hz |
|
| 0.00080 @Frequency 1e+6 Hz |
0.00080 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 200 V | 200 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | |
| Vicat Softening Point | 130 °C | 266 °F | 50°C/hr/50 N |