| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 | ||
| Water Absorption | 7.0 % | 7.0 % | ISO 62 | ||
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 160 MPa | 23200 psi | conditioned; ISO 2039-1 | ||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | conditioned; ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | ||
| Elongation at Yield | 6.0 % | 6.0 % | conditioned; ISO 527-1/-2 | ||
| Tensile Modulus | 2.80 GPa | 406 ksi | conditioned; ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB | NB | conditioned; ISO 179/1eU | ||
 |
NB @Temperature 30.0 °C |
NB @Temperature 86.0 °F |
conditioned; ISO 179/1eU | ||
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | conditioned; ISO 179/1eA | ||
| |
1.20 J/cm² @Temperature 30.0 °C |
5.71 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | conditioned; IEC 60243-1 | ||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1/-2 | ||
| Maximum Service Temperature, Air | 80.0 - 100 °C | 176 - 212 °F | long term; EMS | ||
| 120 °C | 248 °F | short term; EMS | |||
| Transformation Temperature, Tg | 160 °C | 320 °F | 10°C/min; ISO 11357-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-2 | V-2 | IEC 60695-11-10 | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified | ||
| De |
|||||
| Automotive | Automotive electr. and electronics, lighting | ||||
| Compressed air systems | |||||
| Cooling and climate control | |||||
| Fuel systems | |||||
| Interior | |||||
| Powertrain and Chassis | |||||
| Electricals & Electronics | Connectors | ||||
| Electrical appliances | |||||
| Electrical equipment | |||||
| Energy distribution | |||||
| Lighting | |||||
| Mobile phones and other portable devices | |||||
| Form | Granules | ||||
| Industry & Consumer goods | Medical devices | ||||
| Packaging | Injectionstretchblowmoulded containers | ||||
| Processing | Calandering | ||||
| Injection Molding | |||||
| Product Attributes | Barrier Properties | ||||
| Co Polyamide | |||||
| Hydrolysis resistant | |||||
| Partially aromatic Polyamide | |||||
| Transparent Polyamide | |||||