Physical Properties Metric English Comments
Density  1.51 g/cc 0.0546 lb/in³ DAM; ISO 1183
Water Absorption  0.45 %
@Thickness 2.00 mm		 0.45 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  0.180 %
@Thickness 2.00 mm		 0.180 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Linear Mold Shrinkage, Flow  0.0050 cm/cm 0.0050 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0090 cm/cm 0.0090 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  58.0 MPa 8410 psi 50%RH; ISO 527-1/-2
  92.0 MPa 13300 psi DAM; ISO 527-1/-2
Tensile Stress   5.36 MPa
@Strain 0.400 %,
Temperature 150 °C		 777 psi
@Strain 0.400 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  8.33 MPa
@Strain 0.500 %,
Temperature 150 °C		 1210 psi
@Strain 0.500 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  9.50 MPa
@Strain 0.800 %,
Temperature 150 °C		 1380 psi
@Strain 0.800 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  10.36 MPa
@Strain 0.100 %,
Temperature -40.0 °C		 1503 psi
@Strain 0.100 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  12.5 MPa
@Strain 0.800 %,
Temperature 150 °C		 1810 psi
@Strain 0.800 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  18.42 MPa
@Strain 0.200 %,
Temperature 23.0 °C		 2672 psi
@Strain 0.200 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  18.92 MPa
@Strain 1.50 %,
Temperature 150 °C		 2744 psi
@Strain 1.50 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  18.98 MPa
@Strain 2.70 %,
Temperature 150 °C		 2753 psi
@Strain 2.70 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  19.85 MPa
@Strain 0.200 %,
Temperature 0.000 °C		 2879 psi
@Strain 0.200 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  20.13 MPa
@Strain 0.200 %,
Temperature 0.000 °C		 2920 psi
@Strain 0.200 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  22.57 MPa
@Strain 4.70 %,
Temperature 150 °C		 3274 psi
@Strain 4.70 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  23.65 MPa
@Strain 2.40 %,
Temperature 150 °C		 3430 psi
@Strain 2.40 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  25.37 MPa
@Strain 0.500 %,
Temperature 23.0 °C		 3680 psi
@Strain 0.500 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  35.71 MPa
@Strain 0.800 %,
Temperature 23.0 °C		 5179 psi
@Strain 0.800 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  42.75 MPa
@Strain 1.10 %,
Temperature 23.0 °C		 6200 psi
@Strain 1.10 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  47.23 MPa
@Strain 1.40 %,
Temperature 23.0 °C		 6850 psi
@Strain 1.40 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  48.0 MPa
@Strain 0.500 %,
Temperature 0.000 °C		 6960 psi
@Strain 0.500 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  53.59 MPa
@Strain 0.600 %,
Temperature 0.000 °C		 7773 psi
@Strain 0.600 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  53.92 MPa
@Strain 0.500 %,
Temperature -40.0 °C		 7820 psi
@Strain 0.500 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  57.8 MPa
@Strain 0.700 %,
Temperature 23.0 °C		 8380 psi
@Strain 0.700 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  58.76 MPa
@Strain 0.600 %,
Temperature -40.0 °C		 8522 psi
@Strain 0.600 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  59.55 MPa
@Strain 8.00 %,
Temperature 23.0 °C		 8637 psi
@Strain 8.00 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  68.01 MPa
@Strain 0.800 %,
Temperature 0.000 °C		 9864 psi
@Strain 0.800 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  70.53 MPa
@Strain 0.900 %,
Temperature 0.000 °C		 10230 psi
@Strain 0.900 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  71.16 MPa
@Strain 1.00 %,
Temperature 23.0 °C		 10320 psi
@Strain 1.00 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  80.05 MPa
@Strain 1.30 %,
Temperature 23.0 °C		 11610 psi
@Strain 1.30 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  80.32 MPa
@Strain 1.20 %,
Temperature 0.000 °C		 11650 psi
@Strain 1.20 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  82.0 MPa
@Strain 0.800 %,
Temperature -40.0 °C		 11900 psi
@Strain 0.800 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  82.42 MPa
@Strain 1.10 %,
Temperature 0.000 °C		 11950 psi
@Strain 1.10 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  82.82 MPa
@Strain 0.900 %,
Temperature -40.0 °C		 12010 psi
@Strain 0.900 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  102.55 MPa
@Strain 1.10 %,
Temperature -40.0 °C		 14874 psi
@Strain 1.10 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  106.14 MPa
@Strain 1.30 %,
Temperature -40.0 °C		 15394 psi
@Strain 1.30 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  117.55 MPa
@Strain 1.50 %,
Temperature -40.0 °C		 17049 psi
@Strain 1.50 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Elongation at Break  2.5 % 2.5 % DAM; ISO 527-1/-2
  8.0 % 8.0 % 50%RH; ISO 527-1/-2
Tensile Modulus  5.40 GPa 783 ksi 50%RH; ISO 527-1/-2
  9.60 GPa 1390 ksi DAM; ISO 527-1/-2
Flexural Modulus  4.80 GPa 696 ksi 50%RH; ISO 178
  9.00 GPa 1310 ksi DAM; ISO 178
Secant Modulus   0.520 GPa
@Strain 6.00 %,
Temperature 100 °C		 75.4 ksi
@Strain 6.00 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  0.543 GPa
@Strain 6.50 %,
Temperature 80.0 °C		 78.7 ksi
@Strain 6.50 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  0.5968 GPa
@Strain 7.50 %,
Temperature 80.0 °C		 86.56 ksi
@Strain 7.50 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  0.645 GPa
@Strain 6.00 %,
Temperature 100 °C		 93.6 ksi
@Strain 6.00 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.855 GPa
@Strain 3.80 %,
Temperature 80.0 °C		 124 ksi
@Strain 3.80 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  1.07 GPa
@Strain 3.00 %,
Temperature 100 °C		 155 ksi
@Strain 3.00 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  1.14 GPa
@Strain 2.20 %,
Temperature 100 °C		 165 ksi
@Strain 2.20 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  1.43 GPa
@Strain 2.60 %,
Temperature 80.0 °C		 208 ksi
@Strain 2.60 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.446 GPa
@Strain 4.00 %,
Temperature 23.0 °C		 209.7 ksi
@Strain 4.00 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  1.45 GPa
@Strain 1.80 %,
Temperature 80.0 °C		 210 ksi
@Strain 1.80 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  1.49 GPa
@Strain 1.70 %,
Temperature 100 °C		 217 ksi
@Strain 1.70 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  1.50 GPa
@Strain 1.40 %,
Temperature 100 °C		 217 ksi
@Strain 1.40 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  1.82 GPa
@Strain 0.900 %,
Temperature 100 °C		 264 ksi
@Strain 0.900 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  1.92 GPa
@Strain 0.900 %,
Temperature 100 °C		 279 ksi
@Strain 0.900 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2.02 GPa
@Strain 0.900 %,
Temperature 80.0 °C		 293 ksi
@Strain 0.900 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2.116 GPa
@Strain 0.500 %,
Temperature 100 °C		 306.9 ksi
@Strain 0.500 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  2.14 GPa
@Strain 1.40 %,
Temperature 80.0 °C		 310 ksi
@Strain 1.40 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  2.226 GPa
@Strain 0.500 %,
Temperature 100 °C		 322.9 ksi
@Strain 0.500 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2.34 GPa
@Strain 0.500 %,
Temperature 80.0 °C		 339 ksi
@Strain 0.500 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2.63 GPa
@Strain 0.900 %,
Temperature 80.0 °C		 382 ksi
@Strain 0.900 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  2.96 GPa
@Strain 1.70 %,
Temperature 23.0 °C		 429 ksi
@Strain 1.70 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.102 GPa
@Strain 0.500 %,
Temperature 80.0 °C		 449.9 ksi
@Strain 0.500 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  3.71 GPa
@Strain 1.20 %,
Temperature 23.0 °C		 538 ksi
@Strain 1.20 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.43 GPa
@Strain 2.00 %,
Temperature 23.0 °C		 643 ksi
@Strain 2.00 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  4.46 GPa
@Strain 0.800 %,
Temperature 23.0 °C		 647 ksi
@Strain 0.800 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.71 GPa
@Strain 1.90 %,
Temperature 0.000 °C		 683 ksi
@Strain 1.90 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.074 GPa
@Strain 0.500 %,
Temperature 23.0 °C		 735.9 ksi
@Strain 0.500 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  5.52 GPa
@Strain 1.80 %,
Temperature 0.000 °C		 800 ksi
@Strain 1.80 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.586 GPa
@Strain 1.50 %,
Temperature 23.0 °C		 810.2 ksi
@Strain 1.50 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  6.03 GPa
@Strain 1.40 %,
Temperature 0.000 °C		 875 ksi
@Strain 1.40 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  6.56 GPa
@Strain 1.90 %,
Temperature -40.0 °C		 952 ksi
@Strain 1.90 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  6.78 GPa
@Strain 1.10 %,
Temperature 23.0 °C		 983 ksi
@Strain 1.10 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  6.84 GPa
@Strain 1.30 %,
Temperature 0.000 °C		 992 ksi
@Strain 1.30 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  6.88 GPa
@Strain 1.80 %,
Temperature -40.0 °C		 999 ksi
@Strain 1.80 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  7.431 GPa
@Strain 1.00 %,
Temperature 0.000 °C		 1078 ksi
@Strain 1.00 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  7.596 GPa
@Strain 1.50 %,
Temperature -40.0 °C		 1102 ksi
@Strain 1.50 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  8.16 GPa
@Strain 0.900 %,
Temperature 0.000 °C		 1180 ksi
@Strain 0.900 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  8.26 GPa
@Strain 0.700 %,
Temperature 23.0 °C		 1200 ksi
@Strain 0.700 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  8.93 GPa
@Strain 0.600 %,
Temperature 0.000 °C		 1300 ksi
@Strain 0.600 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  8.96 GPa
@Strain 1.20 %,
Temperature -40.0 °C		 1300 ksi
@Strain 1.20 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  8.978 GPa
@Strain 1.00 %,
Temperature -40.0 °C		 1302 ksi
@Strain 1.00 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  9.21 GPa
@Strain 0.200 %,
Temperature 23.0 °C		 1340 ksi
@Strain 0.200 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  9.60 GPa
@Strain 0.500 %,
Temperature 0.000 °C		 1390 ksi
@Strain 0.500 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  9.79 GPa
@Strain 0.600 %,
Temperature -40.0 °C		 1420 ksi
@Strain 0.600 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  9.925 GPa
@Strain 0.200 %,
Temperature 0.000 °C		 1440 ksi
@Strain 0.200 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  10.065 GPa
@Strain 0.200 %,
Temperature 0.000 °C		 1459.8 ksi
@Strain 0.200 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  10.25 GPa
@Strain 0.800 %,
Temperature -40.0 °C		 1487 ksi
@Strain 0.800 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  10.36 GPa
@Strain 0.100 %,
Temperature -40.0 °C		 1503 ksi
@Strain 0.100 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  10.784 GPa
@Strain 0.500 %,
Temperature -40.0 °C		 1564.1 ksi
@Strain 0.500 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  3.50 kJ/m² 1.67 ft-lb/in² DAM; ISO 180/1A
  4.00 kJ/m² 1.90 ft-lb/in² 50%RH; ISO 180/1A
  2.00 kJ/m²
@Temperature -30.0 °C		 0.952 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
  2.00 kJ/m²
@Temperature -40.0 °C		 0.952 ft-lb/in²
@Temperature -40.0 °F		 50%RH; ISO 180/1A
  2.50 kJ/m²
@Temperature -40.0 °C		 1.19 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1A
  2.50 kJ/m²
@Temperature -30.0 °C		 1.19 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)  25.0 kJ/m² 11.9 ft-lb/in² DAM; ISO 180/1U
  40.0 kJ/m² 19.0 ft-lb/in² 50%RH; ISO 180/1U
  18.0 kJ/m²
@Temperature -30.0 °C		 8.57 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1U
  18.0 kJ/m²
@Temperature -30.0 °C		 8.57 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1U
Charpy Impact Unnotched  2.50 J/cm² 11.9 ft-lb/in² DAM; ISO 179/1eU
  4.00 J/cm² 19.0 ft-lb/in² 50%RH; ISO 179/1eU
  1.70 J/cm²
@Temperature -30.0 °C		 8.09 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
  1.80 J/cm²
@Temperature -30.0 °C		 8.57 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
Charpy Impact, Notched  0.300 J/cm² 1.43 ft-lb/in² DAM; ISO 179/1eA
  0.300 J/cm² 1.43 ft-lb/in² 50%RH; ISO 179/1eA
  0.200 J/cm²
@Temperature -30.0 °C		 0.952 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
  0.200 J/cm²
@Temperature -30.0 °C		 0.952 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
  0.200 J/cm²
@Temperature -40.0 °C		 0.952 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 179/1eA
  0.200 J/cm²
@Temperature -40.0 °C		 0.952 ft-lb/in²
@Temperature -40.0 °F		 50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour  2500 MPa
@Time 3600 sec		 363000 psi
@Time 1.00 hour		 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours  1600 MPa
@Time 3.60e+6 sec		 232000 psi
@Time 1000 hour		 50%RH; ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm DAM; IEC 60093
Surface Resistance  1.00e+15 ohm 1.00e+15 ohm 50%RH; IEC 60093
Dielectric Strength  30.0 kV/mm 762 kV/in DAM; IEC 60243-1
Dissipation Factor   0.0020
@Frequency 100 Hz		 0.0020
@Frequency 100 Hz		 DAM; IEC 60250
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  36.0 µm/m-°C 20.0 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  66.0 µm/m-°C 36.7 µin/in-°F DAM; ISO 11359-1/-2
Melting Point  263 °C 505 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  245 °C 473 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  205 °C 401 °F DAM; ISO 75-1/-2
Flammability, UL94  HB
@Thickness 0.700 mm		 HB
@Thickness 0.0276 in		 DAM; IEC 60695-11-10
Oxygen Index  23 % 23 % DAM; ISO 4589-1/-2
 
Descriptive Properties
Part Marking Code >PA66-MD40< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  North America  
  South and Central America  
Resin Identification PA66-MD40  

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40305.html

免责声明: 本文 PA66/美国杜邦/10B40 NC010/注塑级/增强级 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4