PPS 10% GF 的物性表：| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 - 2.12 g/cc | 0.0499 - 0.0766 lb/in³ | Average value: 1.66 g/cc Grade Count:37 |
| Filler Content | 5.00 - 10.0 % | 5.00 - 10.0 % | Average value: 8.75 % Grade Count:8 |
| Water Absorption | 0.0200 - 0.200 % | 0.0200 - 0.200 % | Average value: 0.0853 % Grade Count:32 |
| Linear Mold Shrinkage | 0.000500 - 0.0130 cm/cm | 0.000500 - 0.0130 in/in | Average value: 0.00447 cm/cm Grade Count:37 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 - 121 | 100 - 121 | Average value: 114 Grade Count:3 |
| Tensile Strength, Ultimate | 34.5 - 180 MPa | 5000 - 26100 psi | Average value: 93.7 MPa Grade Count:36 |
| Elongation at Break | 0.800 - 3.00 % | 0.800 - 3.00 % | Average value: 1.23 % Grade Count:9 |
| Elongation at Yield | 0.600 - 4.00 % | 0.600 - 4.00 % | Average value: 1.54 % Grade Count:28 |
| Modulus of Elasticity | 5.00 - 23.0 GPa | 725 - 3340 ksi | Average value: 11.4 GPa Grade Count:36 |
| Flexural Yield Strength | 68.9 - 260 MPa | 10000 - 37700 psi | Average value: 139 MPa Grade Count:37 |
| Flexural Modulus | 4.00 - 20.0 GPa | 580 - 2900 ksi | Average value: 9.89 GPa Grade Count:37 |
| Izod Impact, Notched | 0.374 - 0.587 J/cm | 0.700 - 1.10 ft-lb/in | Average value: 0.486 J/cm Grade Count:9 |
| Izod Impact, Unnotched | 0.908 - 2.14 J/cm | 1.70 - 4.00 ft-lb/in | Average value: 1.43 J/cm Grade Count:8 |
| Charpy Impact Unnotched | 0.500 - 4.30 J/cm² | 2.38 - 20.5 ft-lb/in² | Average value: 1.94 J/cm² Grade Count:28 |
| Charpy Impact, Notched | 0.300 - 1.20 J/cm² | 1.43 - 5.71 ft-lb/in² | Average value: 0.688 J/cm² Grade Count:8 |
| Coefficient of Friction | 0.200 - 0.280 | 0.200 - 0.280 | Average value: 0.216 Grade Count:5 |
| Coefficient of Friction, Static | 0.150 - 0.350 | 0.150 - 0.350 | Average value: 0.190 Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 - 1.00e+16 ohm-cm | 1.00e+15 - 1.00e+16 ohm-cm | Average value: 7.75e+15 ohm-cm Grade Count:4 |
| Surface Resistance | 1.00e+10 - 1.00e+14 ohm | 1.00e+10 - 1.00e+14 ohm | Average value: 1.08e+13 ohm Grade Count:10 |
| Insulation Resistance | 1.00e+10 - 1.00e+14 ohm | 1.00e+10 - 1.00e+14 ohm | Average value: 4.50e+12 ohm Grade Count:28 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 19.8 - 41.4 µm/m-°C | 11.0 - 23.0 µin/in-°F | Average value: 27.0 µm/m-°C Grade Count:9 |
| Thermal Conductivity | 0.303 - 8.00 W/m-K | 2.10 - 55.5 BTU-in/hr-ft²-°F | Average value: 2.00 W/m-K Grade Count:13 |
| Maximum Service Temperature, Air | 200 - 240 °C | 392 - 464 °F | Average value: 229 °C Grade Count:28 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 - 282 °C | 500 - 540 °F | Average value: 267 °C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 193 - 271 °C | 380 - 520 °F | Average value: 250 °C Grade Count:22 |
| Vicat Softening Point | 215 - 240 °C | 419 - 464 °F | Average value: 235 °C Grade Count:5 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:25 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 288 - 330 °C | 550 - 626 °F | Average value: 328 °C Grade Count:31 |
| Nozzle Temperature | 320 - 340 °C | 608 - 644 °F | Average value: 330 °C Grade Count:28 |
| Melt Temperature | 300 - 340 °C | 572 - 644 °F | Average value: 320 °C Grade Count:33 |
| Mold Temperature | 135 - 180 °C | 275 - 356 °F | Average value: 163 °C Grade Count:36 |
| Drying Temperature | 50.0 - 149 °C | 122 - 300 °F | Average value: 99.4 °C Grade Count:33 |
| Moisture Content | 0.0400 % | 0.0400 % | Average value: 0.0400 % Grade Count:5 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:8 |