  4. 注塑级 高抗冲PBT/美国杜邦/HR5315HF NC010

注塑级 高抗冲PBT/美国杜邦/HR5315HF NC010

注塑级 高抗冲PBT/美国杜邦/HR5315HF NC010
 参考图片：

颗粒图片：

包装图片：

成品图片：


 

 

 
Physical Properties Metric English Comments
Density  1.14 g/cc 0.0412 lb/in³  
  1.37 g/cc 0.0495 lb/in³ ISO 1183
Water Absorption  0.40 %
@Thickness 2.00 mm		 0.40 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.150 %
@Thickness 2.00 mm		 0.150 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   55190 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 55190 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  63820 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 63820 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  74630 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 74630 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  167300 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 167300 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  195800 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 195800 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  231200 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 231200 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Viscosity Test  95 cm³/g 95 cm³/g ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0050 cm/cm 0.0050 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.011 cm/cm 0.011 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Hardness, Rockwell R  115 115 ISO 2039-2
Tensile Strength at Break  95.0 MPa 13800 psi ISO 527-1/-2
Tensile Stress   9.14 MPa
@Strain 0.550 %,
Temperature 150 °C		 1330 psi
@Strain 0.550 %,
Temperature 302 °F		 ISO 11403-1 -2
  9.58 MPa
@Strain 0.390 %,
Temperature 90.0 °C		 1390 psi
@Strain 0.390 %,
Temperature 194 °F		 ISO 11403-1 -2
  18.33 MPa
@Strain 0.430 %,
Temperature 40.0 °C		 2659 psi
@Strain 0.430 %,
Temperature 104 °F		 ISO 11403-1 -2
  20.5 MPa
@Strain 0.360 %,
Temperature 23.0 °C		 2970 psi
@Strain 0.360 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  22.0 MPa
@Strain 1.71 %,
Temperature 150 °C		 3190 psi
@Strain 1.71 %,
Temperature 302 °F		 ISO 11403-1 -2
  25.93 MPa
@Strain 1.20 %,
Temperature 90.0 °C		 3761 psi
@Strain 1.20 %,
Temperature 194 °F		 ISO 11403-1 -2
  29.54 MPa
@Strain 2.90 %,
Temperature 150 °C		 4284 psi
@Strain 2.90 %,
Temperature 302 °F		 ISO 11403-1 -2
  34.29 MPa
@Strain 4.13 %,
Temperature 150 °C		 4973 psi
@Strain 4.13 %,
Temperature 302 °F		 ISO 11403-1 -2
  37.28 MPa
@Strain 2.01 %,
Temperature 90.0 °C		 5407 psi
@Strain 2.01 %,
Temperature 194 °F		 ISO 11403-1 -2
  41.59 MPa
@Strain 8.81 %,
Temperature 150 °C		 6032 psi
@Strain 8.81 %,
Temperature 302 °F		 ISO 11403-1 -2
  42.9 MPa
@Strain 1.14 %,
Temperature 40.0 °C		 6220 psi
@Strain 1.14 %,
Temperature 104 °F		 ISO 11403-1 -2
  46.08 MPa
@Strain 2.98 %,
Temperature 90.0 °C		 6683 psi
@Strain 2.98 %,
Temperature 194 °F		 ISO 11403-1 -2
  55.57 MPa
@Strain 1.06 %,
Temperature 23.0 °C		 8060 psi
@Strain 1.06 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  57.4 MPa
@Strain 1.72 %,
Temperature 40.0 °C		 8330 psi
@Strain 1.72 %,
Temperature 104 °F		 ISO 11403-1 -2
  64.13 MPa
@Strain 1.17 %,
Temperature 0.000 °C		 9301 psi
@Strain 1.17 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  69.5 MPa
@Strain 2.41 %,
Temperature 40.0 °C		 10100 psi
@Strain 2.41 %,
Temperature 104 °F		 ISO 11403-1 -2
  72.53 MPa
@Strain 1.48 %,
Temperature 23.0 °C		 10520 psi
@Strain 1.48 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  73.93 MPa
@Strain 1.26 %,
Temperature -40.0 °C		 10720 psi
@Strain 1.26 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  81.35 MPa
@Strain 1.54 %,
Temperature -20.0 °C		 11800 psi
@Strain 1.54 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  83.86 MPa
@Strain 1.61 %,
Temperature 0.000 °C		 12160 psi
@Strain 1.61 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  88.48 MPa
@Strain 2.02 %,
Temperature 23.0 °C		 12830 psi
@Strain 2.02 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  100.33 MPa
@Strain 2.09 %,
Temperature 0.000 °C		 14552 psi
@Strain 2.09 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  102.47 MPa
@Strain 2.03 %,
Temperature -20.0 °C		 14862 psi
@Strain 2.03 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  108.32 MPa
@Strain 1.89 %,
Temperature -40.0 °C		 15711 psi
@Strain 1.89 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  114.02 MPa
@Strain 2.69 %,
Temperature 0.000 °C		 16537 psi
@Strain 2.69 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  120.82 MPa
@Strain 2.59 %,
Temperature -20.0 °C		 17523 psi
@Strain 2.59 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  135.83 MPa
@Strain 3.28 %,
Temperature -20.0 °C		 19701 psi
@Strain 3.28 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  136.63 MPa
@Strain 2.53 %,
Temperature -40.0 °C		 19817 psi
@Strain 2.53 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  10.0 MPa
@Strain 0.210 %,
Time 360000 sec		 1450 psi
@Strain 0.210 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.240 %,
Time 3.60e+6 sec		 1450 psi
@Strain 0.240 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.180 %,
Time 3600 sec		 1450 psi
@Strain 0.180 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.190 %,
Time 36000 sec		 1450 psi
@Strain 0.190 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
Elongation at Break  3.0 % 3.0 % ISO 527-1/-2
Tensile Modulus  5.20 GPa 754 ksi ISO 527-1/-2
  1.484 GPa
@Temperature 170 °C		 215.2 ksi
@Temperature 338 °F		 Dynamic; ISO 11403-1 -2
  1.917 GPa
@Temperature 120 °C		 278.0 ksi
@Temperature 248 °F		 ISO 11403-1 -2
  1.985 GPa
@Temperature 110 °C		 287.9 ksi
@Temperature 230 °F		 Dynamic; ISO 11403-1 -2
  3.807 GPa
@Temperature 40.0 °C		 552.2 ksi
@Temperature 104 °F		 ISO 11403-1 -2
  5.113 GPa
@Temperature 30.0 °C		 741.6 ksi
@Temperature 86.0 °F		 Dynamic; ISO 11403-1 -2
  5.524 GPa
@Temperature -20.0 °C		 801.2 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  5.899 GPa
@Temperature -40.0 °C		 855.6 ksi
@Temperature -40.0 °F		 ISO 11403-1 -2
  6.295 GPa
@Temperature -70.0 °C		 913.0 ksi
@Temperature -94.0 °F		 Dynamic; ISO 11403-1 -2
  6.753 GPa
@Temperature -100 °C		 979.4 ksi
@Temperature -148 °F		 Dynamic; ISO 11403-1 -2
Flexural Strength  150 MPa 21800 psi ISO 178
Flexural Modulus  4.70 GPa 682 ksi ISO 178
Shear Modulus   0.6414 GPa
@Temperature 110 °C		 93.03 ksi
@Temperature 230 °F		 Dynamic; ISO 11403-1 -2
  0.8763 GPa
@Temperature 70.0 °C		 127.1 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  1.70 GPa
@Temperature 20.0 °C		 247 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  1.893 GPa
@Temperature -40.0 °C		 274.5 ksi
@Temperature -40.0 °F		 Dynamic; ISO 11403-1 -2
  2.049 GPa
@Temperature -70.0 °C		 297.2 ksi
@Temperature -94.0 °F		 Dynamic; ISO 11403-1 -2
  2.199 GPa
@Temperature -100 °C		 318.9 ksi
@Temperature -148 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   2.58 GPa
@Strain 2.93 %,
Temperature 40.0 °C		 374 ksi
@Strain 2.93 %,
Temperature 104 °F		 ISO 11403-1 -2
  3.18 GPa
@Strain 1.94 %,
Temperature 40.0 °C		 462 ksi
@Strain 1.94 %,
Temperature 104 °F		 ISO 11403-1 -2
  3.76 GPa
@Strain 1.14 %,
Temperature 40.0 °C		 546 ksi
@Strain 1.14 %,
Temperature 104 °F		 ISO 11403-1 -2
  3.82 GPa
@Strain 3.15 %,
Temperature 0.000 °C		 554 ksi
@Strain 3.15 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  3.97 GPa
@Strain 2.44 %,
Temperature 23.0 °C		 575 ksi
@Strain 2.44 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  4.26 GPa
@Strain 0.430 %,
Temperature 40.0 °C		 618 ksi
@Strain 0.430 %,
Temperature 104 °F		 ISO 11403-1 -2
  4.50 GPa
@Strain 2.81 %,
Temperature -20.0 °C		 653 ksi
@Strain 2.81 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  4.61 GPa
@Strain 2.28 %,
Temperature 0.000 °C		 669 ksi
@Strain 2.28 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  4.77 GPa
@Strain 1.64 %,
Temperature 23.0 °C		 692 ksi
@Strain 1.64 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  5.05 GPa
@Strain 2.03 %,
Temperature -20.0 °C		 732 ksi
@Strain 2.03 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  5.2087 GPa
@Strain 1.61 %,
Temperature 0.000 °C		 755.47 ksi
@Strain 1.61 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  5.24 GPa
@Strain 1.06 %,
Temperature 23.0 °C		 760 ksi
@Strain 1.06 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  5.28 GPa
@Strain 1.54 %,
Temperature -20.0 °C		 766 ksi
@Strain 1.54 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  5.32 GPa
@Strain 2.68 %,
Temperature -40.0 °C		 771 ksi
@Strain 2.68 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  5.4812 GPa
@Strain 1.17 %,
Temperature 0.000 °C		 794.99 ksi
@Strain 1.17 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  5.69 GPa
@Strain 0.360 %,
Temperature 23.0 °C		 826 ksi
@Strain 0.360 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  5.73 GPa
@Strain 1.89 %,
Temperature -40.0 °C		 831 ksi
@Strain 1.89 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  5.87 GPa
@Strain 1.26 %,
Temperature -40.0 °C		 851 ksi
@Strain 1.26 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  10.0 kJ/m² 4.76 ft-lb/in² ISO 180/1A
  6.00 kJ/m²
@Temperature -40.0 °C		 2.86 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1A
  10.0 kJ/m²
@Temperature -30.0 °C		 4.76 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  45.0 kJ/m² 21.4 ft-lb/in² ISO 180/1U
  30.0 kJ/m²
@Temperature -40.0 °C		 14.3 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1U
  40.0 kJ/m²
@Temperature -30.0 °C		 19.0 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1U
Charpy Impact Unnotched  6.00 J/cm² 28.6 ft-lb/in² ISO 179/1eU
  3.00 J/cm²
@Temperature -30.0 °C		 14.3 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  1.00 J/cm² 4.76 ft-lb/in² ISO 179/1eA
  0.700 J/cm²
@Temperature -30.0 °C		 3.33 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour   4790 MPa
@Pressure 45.0 MPa,
Temperature 23.0 °C		 694000 psi
@Pressure 6530 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4840 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 702000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5000 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 725000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5230 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 759000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5560 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 806000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5000 MPa
@Time 3600 sec		 725000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours   3210 MPa
@Pressure 45.0 MPa,
Temperature 23.0 °C		 466000 psi
@Pressure 6530 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  3290 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 477000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  3490 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 506000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  3780 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 549000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4170 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 604000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4200 MPa
@Time 3.60e+6 sec		 609000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+14 ohm 1.00e+14 ohm IEC 60093
Dielectric Strength  26.0 kV/mm 660 kV/in IEC 60243-1
Dissipation Factor   0.010
@Frequency 100 Hz		 0.010
@Frequency 100 Hz		 IEC 60250
  0.010
@Frequency 1.00e+6 Hz		 0.010
@Frequency 1.00e+6 Hz		 IEC 60250
  0.010
@Frequency 1.00e+6 Hz		 0.010
@Frequency 1.00e+6 Hz		 ASTM D150
  0.010
@Frequency 100 Hz		 0.010
@Frequency 100 Hz		 ASTM D150
Comparative Tracking Index  325 V 325 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  41.0 µm/m-°C 22.8 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  1.86 J/g-°C 0.445 BTU/lb-°F  
Thermal Conductivity  0.260 W/m-K 1.80 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  220 °C 428 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  200 °C 392 °F ISO 75-1/-2
Glass Transition Temp, Tg  65.0 °C 149 °F 10°C/min; ISO 11357-1/-2
Flammability, UL94  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
Oxygen Index  20 % 20 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT-IGF15< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT-IGF15  

聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(TPA)或者对苯二甲酸酯(DMT)聚缩合而成，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。

⒈优良的机械性能，机械强度高，耐疲劳性和尺寸稳定好。蠕变也小，这些性能在高温条件下也极少有变化。

⒉生产PBT所消耗的能量是工程塑料中最低的的，这对于世界范围内能源紧缺的情况下，具有十分重要的意义。

⒊耐热老化性优异，增强后的UL温度指数达到120~140℃，此外，户外长期老化性也很好。

⒋耐溶剂好，无应力开裂。

⒌PBT易于阻燃，可达UL94V-0级，由于与阻燃剂亲和性能好，所以容易开发反应型或添加型的阻燃品级。阻燃产品在电子电器工业中获得广泛应用。

⒍PBT遇水易分解，在高温、高湿环境下使用需谨慎。

⒎优良的电气性能，体积电阻率及介电强度高，耐电弧性优良，吸湿性极小，在潮湿及高温环境下，也能保持电性能稳定，是制造电子、电器零件的理想材料。

⒏易成型加工和二次加工，易用普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程材料要求低，在加工薄壁制件时仅需几秒钟，对大部件也只需40-60s即可。

PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。

优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；

3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。

用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；

2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；

3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。

特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40418.html

免责声明: 本文 注塑级 高抗冲PBT/美国杜邦/HR5315HF NC010 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4