  4. PBT 美国杜邦 SK601 NC010耐化学 耐老化 耐热

PBT 美国杜邦 SK601 NC010耐化学 耐老化 耐热

PBT 美国杜邦 SK601 NC010 耐化学 耐老化 耐热
 参考图片：

颗粒图片：

10-03-30-95-421529.jpg.middle_副本

包装图片：

成品图片：

8-1031642-801394

 

 

 
Physical Properties Metric English Comments
Density  1.19 g/cc 0.0430 lb/in³  
  1.37 g/cc 0.0495 lb/in³ ISO 1183
Water Absorption  0.40 %
@Thickness 2.00 mm		 0.40 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.200 %
@Thickness 2.00 mm		 0.200 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity  78230 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 78230 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  89660 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 89660 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  103700 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 103700 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  224100 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 224100 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  268600 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 268600 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  323100 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 323100 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Viscosity Test  110 cm³/g 110 cm³/g ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0070 cm/cm 0.0070 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.012 cm/cm 0.012 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  90.0 MPa 13100 psi ISO 527-1/-2
Tensile Stress   3.06 MPa
@Strain 0.250 %,
Temperature 160 °C		 444 psi
@Strain 0.250 %,
Temperature 320 °F		 ISO 11403-1 -2
  8.55 MPa
@Strain 0.250 %,
Temperature 40.0 °C		 1240 psi
@Strain 0.250 %,
Temperature 104 °F		 ISO 11403-1 -2
  11.1 MPa
@Strain 0.250 %,
Temperature 23.0 °C		 1610 psi
@Strain 0.250 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  12.1 MPa
@Strain 0.250 %,
Temperature 0.000 °C		 1750 psi
@Strain 0.250 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  13.2 MPa
@Strain 0.250 %,
Temperature -20.0 °C		 1910 psi
@Strain 0.250 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  13.7 MPa
@Strain 0.250 %,
Temperature -40.0 °C		 1990 psi
@Strain 0.250 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  14.5 MPa
@Strain 1.50 %,
Temperature 160 °C		 2100 psi
@Strain 1.50 %,
Temperature 320 °F		 ISO 11403-1 -2
  21.6 MPa
@Strain 3.00 %,
Temperature 160 °C		 3130 psi
@Strain 3.00 %,
Temperature 320 °F		 ISO 11403-1 -2
  45.5 MPa
@Strain 1.50 %,
Temperature 40.0 °C		 6600 psi
@Strain 1.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  59.5 MPa
@Strain 1.50 %,
Temperature 23.0 °C		 8630 psi
@Strain 1.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  67.0 MPa
@Strain 3.00 %,
Temperature 40.0 °C		 9720 psi
@Strain 3.00 %,
Temperature 104 °F		 ISO 11403-1 -2
  69.2 MPa
@Strain 1.50 %,
Temperature 0.000 °C		 10000 psi
@Strain 1.50 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  72.9 MPa
@Strain 1.50 %,
Temperature -20.0 °C		 10600 psi
@Strain 1.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  75.0 MPa
@Strain 1.50 %,
Temperature -40.0 °C		 10900 psi
@Strain 1.50 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  90.2 MPa
@Strain 3.00 %,
Temperature 23.0 °C		 13100 psi
@Strain 3.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  10.0 MPa
@Strain 0.270 %,
Time 36000 sec		 1450 psi
@Strain 0.270 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.249 %,
Time 3600 sec		 1450 psi
@Strain 0.249 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.398 %,
Time 3.60e+6 sec		 1450 psi
@Strain 0.398 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  25.0 MPa
@Strain 0.730 %,
Time 360000 sec		 3630 psi
@Strain 0.730 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  40.0 MPa
@Strain 1.75 %,
Time 3.60e+6 sec		 5800 psi
@Strain 1.75 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  40.0 MPa
@Strain 1.17 %,
Time 36000 sec		 5800 psi
@Strain 1.17 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Time 3600 sec,
Strain 1.40 %		 7250 psi
@Time 1.00 hour,
Strain 1.40 %		 isochronous; ISO 11403-1 -2
  60.0 MPa
@Strain 2.75 %,
Time 360000 sec		 8700 psi
@Strain 2.75 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
Elongation at Break  4.7 % 4.7 % ISO 527-1/-2
Tensile Modulus  4.50 GPa 653 ksi ISO 527-1/-2
Flexural Strength  140 MPa 20300 psi ISO 178
Shear Modulus   0.288 GPa
@Temperature 160 °C		 41.8 ksi
@Temperature 320 °F		 Dynamic; ISO 11403-1 -2
  0.340 GPa
@Temperature 120 °C		 49.3 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.513 GPa
@Temperature 70.0 °C		 74.4 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  1.24 GPa
@Temperature 20.0 °C		 180 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  1.35 GPa
@Temperature -20.0 °C		 196 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.49 GPa
@Temperature -50.0 °C		 216 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   1.04 GPa
@Strain 3.50 %,
Temperature 100 °C		 151 ksi
@Strain 3.50 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.25 GPa
@Strain 3.50 %,
Temperature 80.0 °C		 181 ksi
@Strain 3.50 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.47 GPa
@Strain 1.50 %,
Temperature 100 °C		 213 ksi
@Strain 1.50 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.57 GPa
@Strain 1.50 %,
Temperature 80.0 °C		 227 ksi
@Strain 1.50 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.66 GPa
@Strain 0.250 %,
Temperature 100 °C		 241 ksi
@Strain 0.250 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.80 GPa
@Strain 0.250 %,
Temperature 80.0 °C		 261 ksi
@Strain 0.250 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.98 GPa
@Strain 3.50 %,
Temperature 40.0 °C		 287 ksi
@Strain 3.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  2.46 GPa
@Strain 3.70 %,
Temperature 23.0 °C		 357 ksi
@Strain 3.70 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  3.03 GPa
@Strain 1.50 %,
Temperature 40.0 °C		 440 ksi
@Strain 1.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  3.42 GPa
@Strain 0.250 %,
Temperature 40.0 °C		 496 ksi
@Strain 0.250 %,
Temperature 104 °F		 ISO 11403-1 -2
  3.97 GPa
@Strain 1.50 %,
Temperature 23.0 °C		 575 ksi
@Strain 1.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  4.44 GPa
@Strain 0.250 %,
Temperature 23.0 °C		 644 ksi
@Strain 0.250 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  4.61 GPa
@Strain 1.50 %,
Temperature 0.000 °C		 669 ksi
@Strain 1.50 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  4.84 GPa
@Strain 0.250 %,
Temperature 0.000 °C		 702 ksi
@Strain 0.250 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  4.86 GPa
@Strain 1.50 %,
Temperature -20.0 °C		 705 ksi
@Strain 1.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  5.00 GPa
@Strain 1.50 %,
Temperature -40.0 °C		 725 ksi
@Strain 1.50 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  5.28 GPa
@Strain 0.250 %,
Temperature -20.0 °C		 766 ksi
@Strain 0.250 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  5.48 GPa
@Strain 0.250 %,
Temperature -40.0 °C		 795 ksi
@Strain 0.250 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  4.50 kJ/m² 2.14 ft-lb/in² ISO 180/1A
  5.00 kJ/m²
@Temperature -30.0 °C		 2.38 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  27.0 kJ/m² 12.8 ft-lb/in² ISO 180/1U
  26.0 kJ/m²
@Temperature -30.0 °C		 12.4 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1U
Charpy Impact Unnotched  4.00 J/cm² 19.0 ft-lb/in² ISO 179/1eU
  4.00 J/cm²
@Temperature -30.0 °C		 19.0 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.600 J/cm² 2.86 ft-lb/in² ISO 179/1eA
  0.600 J/cm²
@Temperature -30.0 °C		 2.86 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour   1030 MPa
@Pressure 25.0 MPa,
Temperature 110 °C		 149000 psi
@Pressure 3630 psi,
Temperature 230 °F		 ISO 11403-1 -2
  1130 MPa
@Pressure 20.0 MPa,
Temperature 110 °C		 164000 psi
@Pressure 2900 psi,
Temperature 230 °F		 ISO 11403-1 -2
  1260.5 MPa
@Pressure 15.0 MPa,
Temperature 110 °C		 182820 psi
@Pressure 2180 psi,
Temperature 230 °F		 ISO 11403-1 -2
  1370 MPa
@Pressure 10.0 MPa,
Temperature 110 °C		 199000 psi
@Pressure 1450 psi,
Temperature 230 °F		 ISO 11403-1 -2
  1430 MPa
@Pressure 5.00 MPa,
Temperature 110 °C		 207000 psi
@Pressure 725 psi,
Temperature 230 °F		 ISO 11403-1 -2
  1562.5 MPa
@Pressure 35.0 MPa,
Temperature 60.0 °C		 226620 psi
@Pressure 5080 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1680 MPa
@Pressure 30.0 MPa,
Temperature 60.0 °C		 243000 psi
@Pressure 4350 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1760 MPa
@Pressure 25.0 MPa,
Temperature 60.0 °C		 255000 psi
@Pressure 3630 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1801.8 MPa
@Pressure 20.0 MPa,
Temperature 60.0 °C		 261330 psi
@Pressure 2900 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1850 MPa
@Pressure 15.0 MPa,
Temperature 60.0 °C		 269000 psi
@Pressure 2180 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1870 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 271000 psi
@Pressure 1450 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1890 MPa
@Pressure 5.00 MPa,
Temperature 60.0 °C		 274000 psi
@Pressure 725 psi,
Temperature 140 °F		 ISO 11403-1 -2
  3000 MPa
@Pressure 60.0 MPa,
Temperature 23.0 °C		 435000 psi
@Pressure 8700 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  3570 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 518000 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  3850 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 558000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  3970 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 576000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4020 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 582000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4030 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 584000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4000 MPa
@Time 3600 sec		 580000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours   880 MPa
@Pressure 25.0 MPa,
Temperature 110 °C		 128000 psi
@Pressure 3630 psi,
Temperature 230 °F		 ISO 11403-1 -2
  975.61 MPa
@Pressure 20.0 MPa,
Temperature 110 °C		 141500 psi
@Pressure 2900 psi,
Temperature 230 °F		 ISO 11403-1 -2
  1110 MPa
@Pressure 15.0 MPa,
Temperature 110 °C		 161000 psi
@Pressure 2180 psi,
Temperature 230 °F		 ISO 11403-1 -2
  1243.2 MPa
@Pressure 10.0 MPa,
Temperature 110 °C		 180310 psi
@Pressure 1450 psi,
Temperature 230 °F		 ISO 11403-1 -2
  1310 MPa
@Pressure 35.0 MPa,
Temperature 60.0 °C		 190000 psi
@Pressure 5080 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1330 MPa
@Pressure 5.00 MPa,
Temperature 110 °C		 193000 psi
@Pressure 725 psi,
Temperature 230 °F		 ISO 11403-1 -2
  1470 MPa
@Pressure 30.0 MPa,
Temperature 60.0 °C		 213000 psi
@Pressure 4350 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1560 MPa
@Pressure 25.0 MPa,
Temperature 60.0 °C		 226000 psi
@Pressure 3630 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1574.8 MPa
@Pressure 20.0 MPa,
Temperature 60.0 °C		 228410 psi
@Pressure 2900 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1612.9 MPa
@Pressure 15.0 MPa,
Temperature 60.0 °C		 233930 psi
@Pressure 2180 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1620 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 235000 psi
@Pressure 1450 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1640 MPa
@Pressure 5.00 MPa,
Temperature 60.0 °C		 238000 psi
@Pressure 725 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1734.1 MPa
@Pressure 60.0 MPa,
Temperature 23.0 °C		 251510 psi
@Pressure 8700 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2090 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 303000 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2290 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 332000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2400 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 348000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2470 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 358000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2510 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 364000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2500 MPa
@Time 3.60e+6 sec		 363000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Dielectric Constant   3.5
@Frequency 1.00e+6 Hz		 3.5
@Frequency 1.00e+6 Hz		 IEC 60250
  3.9
@Frequency 100 Hz		 3.9
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  30.0 kV/mm 762 kV/in IEC 60243-1
Dissipation Factor   0.0020
@Frequency 100 Hz		 0.0020
@Frequency 100 Hz		 IEC 60250
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  300 V 300 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  60.0 µm/m-°C 33.3 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  120 µm/m-°C 66.7 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  1.89 J/g-°C 0.452 BTU/lb-°F  
Thermal Conductivity  0.240 W/m-K 1.67 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  215 °C 419 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  175 °C 347 °F ISO 75-1/-2
Vicat Softening Point  205 °C 401 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Flame Spread  36 mm/min
@Thickness 1.00 mm		 1.4 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
Oxygen Index  20 % 20 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT-GF10< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT-GF10  
UL recognition UL  

聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(TPA)或者对苯二甲酸酯(DMT)聚缩合而成，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。

⒈优良的机械性能，机械强度高，耐疲劳性和尺寸稳定好。蠕变也小，这些性能在高温条件下也极少有变化。

⒉生产PBT所消耗的能量是工程塑料中最低的的，这对于世界范围内能源紧缺的情况下，具有十分重要的意义。

⒊耐热老化性优异，增强后的UL温度指数达到120~140℃，此外，户外长期老化性也很好。

⒋耐溶剂好，无应力开裂。

⒌PBT易于阻燃，可达UL94V-0级，由于与阻燃剂亲和性能好，所以容易开发反应型或添加型的阻燃品级。阻燃产品在电子电器工业中获得广泛应用。

⒍PBT遇水易分解，在高温、高湿环境下使用需谨慎。

⒎优良的电气性能，体积电阻率及介电强度高，耐电弧性优良，吸湿性极小，在潮湿及高温环境下，也能保持电性能稳定，是制造电子、电器零件的理想材料。

⒏易成型加工和二次加工，易用普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程材料要求低，在加工薄壁制件时仅需几秒钟，对大部件也只需40-60s即可。

PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。

优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；

3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。

用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；

2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；

3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。

特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40444.html

免责声明: 本文 PBT 美国杜邦 SK601 NC010耐化学 耐老化 耐热 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4