类别：聚合物；薄膜；热塑性；聚乙烯（PE）；聚乙烯；线性低密度聚乙烯（LLDPE），注射成型
材料说明：聚乙烯®GA 601系列是颗粒状的，线性低密度聚乙烯的最大强度和韧性要求的应用。这些产品提供优良的添加剂均匀性，不需要转移设备的修改，并促进清洁和安全处理。应用范围包括重型运输袋，总理衬垫，商业和工业包装，以及食品和消费包装。
图：
物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 38.1 microns | 1.50 mil | 2.5:1 BUR | ||
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 | ||
| Film Elongation at Break, TD | 625 % | 625 % | ASTM D882 | ||
| Dart Drop, Total Energy | 2.44 J | 1.80 ft-lb | ASTM D4272 | ||
| Elmendorf Tear Strength MD | 600 g | 600 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 900 g | 900 g | ASTM D1922 | ||
| Dart dro Test | 290 g | 0.639 lb | F50; ASTM D1709A | ||
| Film Tensile Strength at Break, MD | 36.5 MPa | 5300 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 207 MPa | 30000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 238 MPa | 34500 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 12 % | 12 % | ASTM D1003 | ||
| Gloss | 50 % | 50 % | 45°; ASTM D2457 | ||
| De |
|||||
| Antiblock | High | ||||
| Slip | None | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com