| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H. | ||
| Viscosity Test | 105 cm³/g | 105 cm³/g | Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Sheet | ||
| 0.0029 cm/cm | 0.0029 in/in | 60x60x2mm; ISO 294 | |||
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | 60x60x2mm; ISO 294 | ||
| 0.0075 cm/cm | 0.0075 in/in | Sheet | |||
| Melt Flow | 23.9 g/10 min @Load 2.16 kg, Temperature 275 °C |
23.9 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 164 MPa | 23800 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 125 MPa | 18100 psi | 5mm/min; ISO 527-2 | ||
| Tensile Strength | 65.0 MPa @Temperature 100 °C |
9430 psi @Temperature 212 °F |
ISO 527 | ||
| 120 MPa @Temperature 50.0 °C |
17400 psi @Temperature 122 °F |
ISO 527 | |||
| 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
ISO 527 | |||
| 195 MPa @Temperature -40.0 °C |
28300 psi @Temperature -40.0 °F |
ISO 527 | |||
| Elongation at Break | 2.2 % | 2.2 % | 5mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 9.70 GPa | 1410 ksi | ISO 527-2 | ||
| Flexural Strength | 183 MPa | 26500 psi | ISO 178 | ||
| Charpy Impact Unnotched | 5.90 J/cm² | 28.1 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA | ||
| Dart Drop, Total Energy | <= 5.00 J | <= 3.69 ft-lb | ISO 6603-1 | ||
| Tensile Creep Modulus, 1000 hours | 6700 MPa | 972000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.00e+15 ohm-cm | 3.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 95.0 kV/mm | 2410 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 | ||
| 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 125 V | 125 V | Test solution B; IEC 60112 | ||
| 500 V | 500 V | Test solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 3.00 µm/m-°C @Temperature 23.0 - 80.0 °C |
1.67 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | IEC 1006 | ||
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | |||
| Maximum Service Temperature, Air | 110 °C | 230 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 140 °C | 284 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |||
| 170 °C | 338 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ISO 75-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
||||
| Flame Spread | <= 100 mm/min | <= 3.94 in/min | DIN 75200 | ||
| Glow Wire Test | 760 °C @Thickness 3.00 mm |
1400 °F @Thickness 0.118 in |
IEC 695 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection molding | ||
| 270 °C | 518 °F | for shrinkage test | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| 80.0 °C | 176 °F | for shrinkage test | |||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| Lubricant | |||||
| U.V. stabilized or stable to weather | |||||
概述
聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(TPA)或者对苯二甲酸酯(DMT)聚缩合而成，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。
化学物质
⒈优良的机械性能，机械强度高，耐疲劳性和尺寸稳定好。蠕变也小，这些性能在高温条件下也极少有变化。
⒉生产PBT所消耗的能量是工程塑料中最低的的，这对于世界范围内能源紧缺的情况下，具有十分重要的意义。
⒊耐热老化性优异，增强后的UL温度指数达到120~140℃，此外，户外长期老化性也很好。
⒋耐溶剂好，无应力开裂。
⒌PBT易于阻燃，可达UL94V-0级，由于与阻燃剂亲和性能好，所以容易开发反应型或添加型的阻燃品级。阻燃产品在电子电器工业中获得广泛应用。
⒍PBT遇水易分解，在高温、高湿环境下使用需谨慎。
⒎优良的电气性能，体积电阻率及介电强度高，耐电弧性优良，吸湿性极小，在潮湿及高温环境下，也能保持电性能稳定，是制造电子、电器零件的理想材料。
⒏易成型加工和二次加工，易用普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程材料要求低，在加工薄壁制件时仅需几秒钟，对大部件也只需40-60s即可。
PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。
优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；
3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。
用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；
2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；
3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。
特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.