聚合物；热塑性；液晶聚合物（LCP）；液晶聚合物（LCP），30%的玻璃纤维填充
LCP HF130 材料说明：
LCP, 30% glass fiber reinforced, HDT ~300°C
LCP HF130 形式：
粒子
LCP HF130 加工方法：
注塑成型
LCP HF130 填料：
玻璃纤维增强材料, 30% 填料按重量
LCP HF130 的物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.040 % | 0.040 % | similar to ISO 62 test | ||
| Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0046 cm/cm | 0.0046 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 136 MPa | 19700 psi | ISO 527-1 | ||
| Elongation at Break | 1.5 % | 1.5 % | ISO 527-1 | ||
| Tensile Modulus | 14.0 GPa | 2030 ksi | ISO 527-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 305 °C | 581 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL Registered; IEC 60695-11-10 | ||
| De |
|||||
| Resin Type | LCP-GF30 | ||||