LCP D5506 材料说明：D系列CoolPoly导热塑料传热特性，一个以前没有的注塑级聚合物。CoolPoly是轻量级的，网状可塑性、允许应用以前仅限于金属设计的自由。D系列是不导电的，可用于其介电性能。
D5506是CoolPoly导热树脂注塑基于液晶聚合物。d5506 CoolPoly电绝缘。像CoolPoly导热聚合物d5506酷比标准的注塑级树脂更快。
LCP D5506 形式：粒子
LCP D5506 加工方法：注塑成型
LCP D5506 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D551 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ISO 527-1 |
| Elongation at Break | 0.76 % | 0.76 % | ISO 527-1 |
| Tensile Modulus | 10.7 GPa | 1550 ksi | ISO 527-1 |
| Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
| Flexural Modulus | 12.7 GPa | 1840 ksi | ISO 178 |
| Charpy Impact Unnotched | 0.560 J/cm² | 2.67 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.280 J/cm² | 1.33 ft-lb/in² | ISO 179-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.60e+16 ohm-cm | 1.60e+16 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 2.00e+14 ohm | 2.00e+14 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 6.40 µm/m-°C @Temperature 20.0 °C |
3.56 µin/in-°F @Temperature 68.0 °F |
ASTM E831-03 |
| CTE, linear, Transverse to Flow | 11.3 µm/m-°C @Temperature 20.0 °C |
6.28 µin/in-°F @Temperature 68.0 °F |
ASTM E831-03 |
| Specific Heat Capacity | 0.970 J/g-°C | 0.232 BTU/lb-°F | ASTM E1461 |
| Thermal Conductivity | 10.0 W/m-K | 69.4 BTU-in/hr-ft²-°F | ASTM E1461 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 300 °C | >= 572 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 264 °C | 507 °F | ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 330 - 360 °C | 626 - 680 °F | |
| Middle Barrel Temperature | 340 - 370 °C | 644 - 698 °F | |
| Front Barrel Temperature | 345 - 380 °C | 653 - 716 °F | |
| Nozzle Temperature | 350 - 382 °C | 662 - 720 °F | |
| Melt Temperature | 349 - 393 °C | 660 - 739 °F | |
| Mold Temperature | 93.0 - 177 °C | 199 - 351 °F | |
| Drying Temperature | 180 °C | 356 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.010 % | 0.010 % | |
| Dew Point | -34.0 °C | -29.2 °F | |
| Injection Pressure | 35.0 - 70.0 MPa | 5080 - 10200 psi | |
| Hold Pressure | 7.00 - 35.0 MPa | 1020 - 5080 psi | |
| Back Pressure | 0.000 - 0.350 MPa | 0.000 - 50.8 psi | |
| Screw Speed | 75 - 150 rpm | 75 - 150 rpm | |