| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.943 g/cc | 0.0341 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 17 - 20 % | 17 - 20 % | Arkema | ||
| Melt Index of Compound | 6.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 84 | 84 | ASTM D2240 | ||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 | ||
| 24.0 MPa | 3480 psi | Film Property, 50 µm thickness; ASTM D882 | |||
| Tensile Strength, Yield | 3.50 MPa | 508 psi | ASTM D638 | ||
| 4.30 MPa | 624 psi | Film Property, 50 µm thickness; ASTM D882 | |||
| Elongation at Break | 600 - 800 % | 600 - 800 % | Film Property, 50 µm thickness; ASTM D882 | ||
| 600 - 900 % | 600 - 900 % | ASTM D638 | |||
| Dart dro Test | 250 g | 0.551 lb | ASTM D1709 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 86.0 °C | 187 °F | DSC | ||
| Vicat Softening Point | 54.0 °C | 129 °F | ASTM D1525 | ||
| Ring & Ball Softening Point | 158 °C | 316 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 2.5 % | 2.5 % | 50 micron film; ASTM D1003 | ||
| De |
|||||
| MAH Mini | 1600 | ||||
图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com