| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.0 % @Thickness 2.00 mm |
1.0 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Moisture Absorption | 0.200 % @Thickness 2.00 mm |
0.200 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Viscosity | 100000 cP @Shear Rate 5000 1/s, Temperature 230 °C |
100000 cP @Shear Rate 5000 1/s, Temperature 446 °F |
ISO 11403-1 -2 | ||
| 107000 cP @Shear Rate 5000 1/s, Temperature 215 °C |
107000 cP @Shear Rate 5000 1/s, Temperature 419 °F |
ISO 11403-1 -2 | |||
| 116000 cP @Shear Rate 5000 1/s, Temperature 200 °C |
116000 cP @Shear Rate 5000 1/s, Temperature 392 °F |
ISO 11403-1 -2 | |||
| 374000 cP @Shear Rate 500 1/s, Temperature 230 °C |
374000 cP @Shear Rate 500 1/s, Temperature 446 °F |
ISO 11403-1 -2 | |||
| 425000 cP @Shear Rate 500 1/s, Temperature 215 °C |
425000 cP @Shear Rate 500 1/s, Temperature 419 °F |
ISO 11403-1 -2 | |||
| 483000 cP @Shear Rate 500 1/s, Temperature 200 °C |
483000 cP @Shear Rate 500 1/s, Temperature 392 °F |
ISO 11403-1 -2 | |||
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-1/-2 | ||
| Tensile Stress | 8.70 MPa @Strain 0.900 %, Temperature 90.0 °C |
1260 psi @Strain 0.900 %, Temperature 194 °F |
ISO 11403-1 -2 | ||
| 21.5 MPa @Strain 3.60 %, Temperature 90.0 °C |
3120 psi @Strain 3.60 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 23.9 MPa @Strain 6.20 %, Temperature 90.0 °C |
3470 psi @Strain 6.20 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 24.3 MPa @Strain 8.90 %, Temperature 90.0 °C |
3520 psi @Strain 8.90 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 27.2 MPa @Strain 1.40 %, Temperature 40.0 °C |
3950 psi @Strain 1.40 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 30.5 MPa @Strain 1.00 %, Temperature 0.000 °C |
4420 psi @Strain 1.00 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 31.6 MPa @Strain 1.20 %, Temperature 23.0 °C |
4580 psi @Strain 1.20 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 32.0 MPa @Strain 0.900 %, Temperature -20.0 °C |
4640 psi @Strain 0.900 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 40.5 MPa @Strain 5.40 %, Temperature 40.0 °C |
5870 psi @Strain 5.40 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 42.2 MPa @Strain 9.40 %, Temperature 40.0 °C |
6120 psi @Strain 9.40 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 42.6 MPa @Strain 13.4 %, Temperature 40.0 °C |
6180 psi @Strain 13.4 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 45.6 MPa @Strain 5.00 %, Temperature 23.0 °C |
6610 psi @Strain 5.00 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 47.3 MPa @Strain 8.70 %, Temperature 23.0 °C |
6860 psi @Strain 8.70 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 47.8 MPa @Strain 12.4 %, Temperature 23.0 °C |
6930 psi @Strain 12.4 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 50.2 MPa @Strain 3.80 %, Temperature 0.000 °C |
7280 psi @Strain 3.80 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 53.7 MPa @Strain 6.60 %, Temperature 0.000 °C |
7790 psi @Strain 6.60 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 54.4 MPa @Strain 9.50 %, Temperature 0.000 °C |
7890 psi @Strain 9.50 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 54.9 MPa @Strain 3.70 %, Temperature -20.0 °C |
7960 psi @Strain 3.70 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 58.2 MPa @Strain 6.50 %, Temperature -20.0 °C |
8440 psi @Strain 6.50 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 59.2 MPa @Strain 9.30 %, Temperature -20.0 °C |
8590 psi @Strain 9.30 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| Elongation at Break | 10 % | 10 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 | ||
| Shear Modulus | 0.141 GPa @Temperature 150 °C |
20.5 ksi @Temperature 302 °F |
Dynamic; ISO 11403-1 -2 | ||
| 0.306 GPa @Temperature 110 °C |
44.4 ksi @Temperature 230 °F |
Dynamic; ISO 11403-1 -2 | |||
| 0.628 GPa @Temperature 60.0 °C |
91.1 ksi @Temperature 140 °F |
Dynamic; ISO 11403-1 -2 | |||
| 0.961 GPa @Temperature 10.0 °C |
139 ksi @Temperature 50.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| 1.12 GPa @Temperature -20.0 °C |
162 ksi @Temperature -4.00 °F |
Dynamic; ISO 11403-1 -2 | |||
| 1.284 GPa @Temperature -50.0 °C |
186.2 ksi @Temperature -58.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| Secant Modulus | 0.396 GPa @Strain 10.7 %, Temperature 40.0 °C |
57.5 ksi @Strain 10.7 %, Temperature 104 °F |
ISO 11403-1 -2 | ||
| 0.481 GPa @Strain 9.90 %, Temperature 23.0 °C |
69.7 ksi @Strain 9.90 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 0.709 GPa @Strain 7.60 %, Temperature 0.000 °C |
103 ksi @Strain 7.60 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 0.750 GPa @Strain 5.40 %, Temperature 40.0 °C |
109 ksi @Strain 5.40 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 0.793 GPa @Strain 7.40 %, Temperature -20.0 °C |
115 ksi @Strain 7.40 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 0.912 GPa @Strain 5.00 %, Temperature 23.0 °C |
132 ksi @Strain 5.00 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 1.32 GPa @Strain 3.80 %, Temperature 0.000 °C |
192 ksi @Strain 3.80 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 1.48 GPa @Strain 3.70 %, Temperature -20.0 °C |
215 ksi @Strain 3.70 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 1.94 GPa @Strain 1.40 %, Temperature 40.0 °C |
282 ksi @Strain 1.40 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 2.63 GPa @Strain 1.20 %, Temperature 23.0 °C |
382 ksi @Strain 1.20 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 3.05 GPa @Strain 1.00 %, Temperature 0.000 °C |
442 ksi @Strain 1.00 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 3.56 GPa @Strain 0.900 %, Temperature -20.0 °C |
516 ksi @Strain 0.900 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU | ||
| 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/1eA | ||
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| Flame Spread | 54 mm/min @Thickness 1.00 mm |
2.1 in/min @Thickness 0.0394 in |
ISO 3795 (FMVSS 302) | ||
| De |
|||||
| Additives | Lubricants | ||||
| Release agent | |||||
| Delivery form | Pellets | ||||
| Part Marking Code | >POM-SF20< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | POM-SF20 | ISO 1043 | |||
| UL recognition | UL | ||||
概述
pom（聚甲醛）
聚甲醛(英文：polyformaldehyde)热塑性结晶聚合物。被誉为“超钢”或者“赛钢”，又称聚氧亚甲基。英文缩写为POM。通常甲醛聚合所得之聚合物，聚合度不高，且易受热解聚。可用作有机化工、合成树脂的原料，也用作药物熏蒸剂。白色可燃结晶粉末，具有甲醛气味。 缓慢溶于冷水，在热水中溶解较快。
一般性能
聚甲醛是一种表面光滑、有光泽的硬而致密的材料，淡黄或白色，薄壁部分呈半透明。燃烧特性为容易燃烧，离火后继续燃烧，火焰上端呈黄色，下端呈蓝色，发生熔融滴落，有强烈的刺激性甲醛味、鱼腥臭。聚甲醛为白色粉末，一般不透明，着色性好，
力学性能
POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。POM的冲击强度较高,POM的摩擦因数小，耐磨性好。POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。
电学性能
POM的电绝缘性较好，几乎不受温度和湿度的影响；介电常数和介电损耗在很宽的温度、湿度和频率范围内变化很小；耐电弧性极好，并可在高温下保持。POM的介电强度与厚度有关，厚度0.127mm时为82.7kV/mm，厚度为1.88mm时为23.6kV/mm。
环境性能
POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。
成形性
结晶料，熔融范围窄，熔融和凝固快，料温稍低于熔融温度即发生结晶，流动性中等，吸湿小，可不经干燥处理。
优缺点
优点
1、具高机械强度和刚性；2、最高的疲劳强度；3、环境抵抗性、耐有机溶剂性佳；
4、耐反覆冲击性强；5、广泛的使用温度范围(-40℃~120℃)；6、良好的电气性质；
7、复原性良好；8、具自已润滑性、耐磨性良好；9、尺寸安定性优。
缺点
受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。
用途
多聚甲醛为高甲醛含量的固态甲醛，呈固体颗粒状、便于贮存和运输。在较高的温度下能变成甲醛蒸气，易于代替高浓度甲醛参与各种反应，有利于化工、制药等化学合成及其他工业领域的应用，特别是在要求使用无水甲醛作原料的合成方面，用途广泛。主要有以下几方面（1）农药：合成乙草胺、丁草胺和草甘膦等；（2）涂料：合成高档汽车用漆；（3）树脂：合成脲醛树脂、酚醛树脂、聚缩醛树脂、蜜胺树脂、离子交换树脂等及各种粘合剂；（4）造纸：合成纸张增强剂； （5）铸造：翻砂脱膜剂、合成铸造粘合剂；（6）养殖业：薰蒸消毒剂。（7）有机原料：用于制备季戊四醇、三羟甲基丙烷、甘油、丙烯酸、丙烯酸甲酯、甲基丙烯酸、N－羟基甲基丙烯酰胺、烷基苯酚、甲基乙烯基酮等。（8）其他：医药及消毒。
上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！
可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：
联系人：邓小姐
联系电话：13917657923
联系QQ:996152797
联系邮箱：996152797@qq.com