类别：聚合物；薄膜；热塑性塑料；乙烯-醋酸乙烯酯
物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM D1505 |
| Water Vapor Transmission | 54.0 g/m²/day | 3.48 g/100 in²/day | 100% Humidity; ASTM F372 |
| Thickness | 50.8 microns | 2.00 mil | 2:1 BUR |
| Melt Flow | 3.1 g/10 min | 3.1 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.7 MPa | 1840 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.20 MPa | 1040 psi | ASTM D882 |
| Film Elongation at Break, MD | 380 % | 380 % | ASTM D882 |
| Film Elongation at Break, TD | 647 % | 647 % | ASTM D882 |
| Film Elongation at Yield, MD | 62 % | 62 % | ASTM D882 |
| Film Elongation at Yield, TD | 64 % | 64 % | ASTM D882 |
| Elmendorf Tear Strength MD | 292 g | 292 g | Notched; ASTM D1922 |
| Elmendorf Tear Strength TD | 232 g | 232 g | Notched; ASTM D1922 |
| Elmendorf Tear Strength, MD | 5.75 g/micron | 146 g/mil | based on 2 mil film; ASTM D1922 |
| Elmendorf Tear Strength, TD | 6.54 g/micron | 166 g/mil | based on 2 mil film; ASTM D1922 |
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.3 MPa | 3230 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 78.0 °C | 172 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | >= 210 °C | >= 410 °F | |
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com