聚合物；热塑性；液晶聚合物（LCP）；液晶聚合物（LCP），30%的玻璃纤维填充
LCP A625 材质说明：
良好的耐磨性。25%石墨填充。
LCP A625 填料/增强材料：
石墨粉, 25% 填料按重量
LCP A625 加工方法：
注塑成型
LCP A625 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 62.0 | 62.0 | ISO 2039-2 |
| Tensile Strength at Break | 140 MPa | 20300 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 5.70 % | 5.70 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 9.00 GPa | 1310 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 |
| Compressive Strength | 56.0 MPa @Strain 1.00 % |
8120 psi @Strain 1.00 % |
ISO 604 |
| Compressive Modulus | 9.00 GPa | 1310 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | ISO 180/1A |
| 62.0 kJ/m² @Temperature 23.0 °C |
29.5 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 6.70 J/cm² | 31.9 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179/1eA |
| Tensile Creep Modulus, 1 hour | 9800 MPa | 1.42e+6 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 7500 MPa | 1.09e+6 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 |
| Dielectric Constant | 13.0 @Frequency 1.00e+6 Hz |
13.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 30.0 @Frequency 100 Hz |
30.0 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0400 @Frequency 100 Hz |
0.0400 @Frequency 100 Hz |
IEC 60250 |
| 0.150 @Frequency 1.00e+6 Hz |
0.150 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 9.00 µm/m-°C | 5.00 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-2 |
| Melting Point | 280 °C | 536 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 114 °C | 237 °F | ISO 75-1, -2 |
| Vicat Softening Point | 159 °C | 318 °F | ISO 306 |
| Flammability, UL94 | V-0 | V-0 | |