| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 5.8 % | 5.8 % | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 7.58 MPa | 1100 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 6.89 MPa | 1000 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 240 % | 240 % | ASTM D882 | ||
| Film Elongation at Break, TD | 670 % | 670 % | ASTM D882 | ||
Impact Test  |
0.813 J @Temperature -34.0 °C |
0.600 ft-lb @Temperature -29.2 °F |
ASTM D4272 | ||
| 2.03 J @Temperature 23.0 °C |
1.50 ft-lb @Temperature 73.4 °F |
ASTM D4272 | |||
| Elmendorf Tear Strength, MD | 8.27 g/micron | 210 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 2.36 g/micron | 60.0 g/mil | ASTM D1922 | ||
| Dart Drop | 4.33 g/micron | 110 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 34.5 MPa | 5000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 22.4 MPa | 3250 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 138 MPa | 20000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 172 MPa | 25000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 103 °C | 217 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.0 % | 3.0 % | ASTM D1003 | ||
| Gloss | 76 % | 76 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified | ||
| De |
|||||
| Features | Thermal Stabilizer | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com