聚合物；热塑性；液晶聚合物（LCP）；液晶聚合物（LCP），30%的玻璃纤维填充
LCP C130 材料说明：
具有性能同样出色的平衡能力和流动温度高容易A130。稍微的尺寸稳定性，在汽相焊比A130。适用于SMT应用红外。30%玻璃增强。
LCP C130 加工方法：
注塑成型
LCP C130 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00400 cm/cm | 0.00400 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80.0 | 80.0 | ISO 2039-2 |
| Tensile Strength at Break | 160 MPa | 23200 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.90 % | 1.90 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 245 MPa | 35500 psi | ISO 178 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178 |
| Compressive Strength | 139 MPa @Strain 1.00 % |
20200 psi @Strain 1.00 % |
ISO 604 |
| Compressive Modulus | 22.0 GPa | 3190 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180/1A |
| 26.0 kJ/m² @Temperature 23.0 °C |
12.4 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 2.80 J/cm² | 13.3 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179/1eA |
| Tensile Creep Modulus, 1 hour | 13600 MPa | 1.97e+6 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 11700 MPa | 1.70e+6 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.70 @Frequency 1.00e+6 Hz |
3.70 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.20 @Frequency 100 Hz |
4.20 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0140 @Frequency 100 Hz |
0.0140 @Frequency 100 Hz |
IEC 60250 |
| 0.0180 @Frequency 1.00e+6 Hz |
0.0180 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Arc Resistance | 182 sec | 182 sec | Internal |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 6.00 µm/m-°C | 3.33 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 18.0 µm/m-°C | 10.0 µin/in-°F | ISO 11359-2 |
| Melting Point | 325 °C | 617 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 211 °C | 412 °F | ISO 75-1, -2 |
| Vicat Softening Point | 192 °C | 378 °F | ISO 306 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 45.0 % | 45.0 % | ISO 4589 |