聚合物；热塑性；液晶聚合物（LCP）；液晶聚合物（LCP），50%的玻璃纤维填充
LCP E150i 材质说明：
使用方便，具有很好的耐热性和机械性能。可以减少相比，e130i一些零件翘曲。50%玻璃纤维增强。
LCP E150i 加工方法：
注塑成型
LCP E150i 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.81 g/cc | 0.0654 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.00600 % | 0.00600 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 66.0 | 66.0 | ISO 2039-2 |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.00 % | 1.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 17.5 GPa | 2540 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 205 MPa | 29700 psi | ISO 178 |
| Flexural Modulus | 18.6 GPa | 2700 ksi | ISO 178 |
| Compressive Strength | 125 MPa @Strain 1.00 % |
18100 psi @Strain 1.00 % |
ISO 604 |
| Compressive Modulus | 18.0 GPa | 2610 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/1A |
| 16.0 kJ/m² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 1.90 J/cm² | 9.04 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 4.70 @Frequency 1.00e+6 Hz |
4.70 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0280 @Frequency 1.00e+6 Hz |
0.0280 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 6.00 µm/m-°C | 3.33 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 17.0 µm/m-°C | 9.44 µin/in-°F | ISO 11359-2 |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 225 °C | 437 °F | ISO 75-1, -2 |
| Vicat Softening Point | 200 °C | 392 °F | ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 @Thickness 0.430 mm |
V-0 @Thickness 0.0169 in |
||