聚合物；热塑性；液晶聚合物（LCP）；液晶聚合物（LCP），40%的玻璃纤维填充
LCP E471i 材质说明：
低翘曲具有优异的性能
LCP E471i 加工方法：
注塑成型
LCP E471i 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.00200 % | 0.00200 % | 23°C/50%RH; ISO 62 |
| Water Absorption at Saturation | 0.0150 % | 0.0150 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 55.0 | 55.0 | ISO 2039-2 |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.50 % | 2.50 % | flexural; ISO 178 |
| 2.50 % | 2.50 % | 5mm/min; ISO 527-2/1A | |
| Tensile Modulus | 13.8 GPa | 2000 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 13.5 GPa | 1960 ksi | ISO 178 |
| Compressive Strength | 82.0 MPa @Strain 1.00 % |
11900 psi @Strain 1.00 % |
ISO 604 |
| Compressive Modulus | 11.0 GPa | 1600 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180/1A |
| 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.80 @Frequency 1.00e+6 Hz |
3.80 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 53.0 kV/mm | 1350 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0310 @Frequency 1.00e+6 Hz |
0.0310 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 6.00 µm/m-°C | 3.33 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 18.0 µm/m-°C | 10.0 µin/in-°F | ISO 11359-2 |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 220 °C | 428 °F | ISO 75-1, -2 |
| Vicat Softening Point | 200 °C | 392 °F | ISO 306 |
| Flammability, UL94 | V-0 | V-0 | |