杜邦高性能聚合物Crastin®sk602 NC010聚对苯二甲酸丁二醇酯（PBT） 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT）；聚对苯二甲酸丁二醇酯（PBT），20%的玻璃纤维填充 材料说明：15%玻璃纤维增强聚对苯二甲酸丁二醇酯 Crastin sk602 NC010是15%玻璃纤维增强聚对苯二甲酸乙二醇酯树脂注塑成型润滑。
 物性表：

 
Physical Properties Metric English Comments
Density  1.22 g/cc 0.0441 lb/in³  
  1.41 g/cc 0.0509 lb/in³ ISO 1183
Water Absorption  0.42 %
@Thickness 2.00 mm		 0.42 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.170 %
@Thickness 2.00 mm		 0.170 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   77750 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 77750 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  90080 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 90080 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  105400 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 105400 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  224600 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 224600 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  274400 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 274400 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  336400 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 336400 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Viscosity Test  105 cm³/g 105 cm³/g ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0040 cm/cm 0.0040 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.011 cm/cm 0.011 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  109 MPa 15800 psi ISO 527-1/-2
Tensile Stress  14.41 MPa
@Strain 0.560 %,
Temperature 90.0 °C		 2090 psi
@Strain 0.560 %,
Temperature 194 °F		 ISO 11403-1 -2
  18.07 MPa
@Strain 0.320 %,
Temperature 23.0 °C		 2621 psi
@Strain 0.320 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  18.34 MPa
@Strain 0.450 %,
Temperature 40.0 °C		 2660 psi
@Strain 0.450 %,
Temperature 104 °F		 ISO 11403-1 -2
  41.62 MPa
@Strain 2.02 %,
Temperature 90.0 °C		 6036 psi
@Strain 2.02 %,
Temperature 194 °F		 ISO 11403-1 -2
  52.91 MPa
@Strain 1.54 %,
Temperature 40.0 °C		 7674 psi
@Strain 1.54 %,
Temperature 104 °F		 ISO 11403-1 -2
  54.86 MPa
@Strain 3.57 %,
Temperature 90.0 °C		 7957 psi
@Strain 3.57 %,
Temperature 194 °F		 ISO 11403-1 -2
  57.84 MPa
@Strain 5.03 %,
Temperature 90.0 °C		 8389 psi
@Strain 5.03 %,
Temperature 194 °F		 ISO 11403-1 -2
  67.19 MPa
@Strain 1.30 %,
Temperature 23.0 °C		 9745 psi
@Strain 1.30 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  77.38 MPa
@Strain 2.80 %,
Temperature 40.0 °C		 11220 psi
@Strain 2.80 %,
Temperature 104 °F		 ISO 11403-1 -2
  83.47 MPa
@Strain 3.88 %,
Temperature 40.0 °C		 12110 psi
@Strain 3.88 %,
Temperature 104 °F		 ISO 11403-1 -2
  97.45 MPa
@Strain 2.25 %,
Temperature 23.0 °C		 14130 psi
@Strain 2.25 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  108.8 MPa
@Strain 3.23 %,
Temperature 23.0 °C		 15780 psi
@Strain 3.23 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  10.0 MPa
@Strain 0.230 %,
Time 3.60e+6 sec		 1450 psi
@Strain 0.230 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.260 %,
Time 3.60e+7 sec		 1450 psi
@Strain 0.260 %,
Time 10000 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.210 %,
Time 360000 sec		 1450 psi
@Strain 0.210 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 0.360 %,
Time 3600 sec		 2900 psi
@Strain 0.360 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 0.390 %,
Time 36000 sec		 2900 psi
@Strain 0.390 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 1.03 %,
Time 36000 sec		 7250 psi
@Strain 1.03 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 0.990 %,
Time 3600 sec		 7250 psi
@Strain 0.990 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 1.62 %,
Time 3.60e+7 sec		 7250 psi
@Strain 1.62 %,
Time 10000 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 1.34 %,
Time 3.60e+6 sec		 7250 psi
@Strain 1.34 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 1.16 %,
Time 360000 sec		 7250 psi
@Strain 1.16 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
Elongation at Break  3.5 % 3.5 % ISO 527-1/-2
Tensile Modulus  5.80 GPa 841 ksi ISO 527-1/-2
Flexural Strength  160 MPa 23200 psi ISO 178
Flexural Modulus  5.20 GPa 754 ksi ISO 178
Shear Modulus   0.328 GPa
@Temperature 160 °C		 47.6 ksi
@Temperature 320 °F		 Dynamic; ISO 11403-1 -2
  0.393 GPa
@Temperature 120 °C		 57.0 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.568 GPa
@Temperature 70.0 °C		 82.4 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  1.42 GPa
@Temperature 20.0 °C		 206 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  1.56 GPa
@Temperature -20.0 °C		 226 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.62 GPa
@Temperature -50.0 °C		 235 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   2.56 GPa
@Strain 3.16 %,
Temperature 40.0 °C		 371 ksi
@Strain 3.16 %,
Temperature 104 °F		 ISO 11403-1 -2
  3.44 GPa
@Strain 1.54 %,
Temperature 40.0 °C		 498 ksi
@Strain 1.54 %,
Temperature 104 °F		 ISO 11403-1 -2
  3.98 GPa
@Strain 2.59 %,
Temperature 23.0 °C		 578 ksi
@Strain 2.59 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  4.08 GPa
@Strain 0.450 %,
Temperature 40.0 °C		 591 ksi
@Strain 0.450 %,
Temperature 104 °F		 ISO 11403-1 -2
  5.17 GPa
@Strain 1.30 %,
Temperature 23.0 °C		 750 ksi
@Strain 1.30 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  5.65 GPa
@Strain 0.320 %,
Temperature 23.0 °C		 819 ksi
@Strain 0.320 %,
Temperature 73.4 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  6.50 kJ/m² 3.09 ft-lb/in² ISO 180/1A
  6.00 kJ/m²
@Temperature -30.0 °C		 2.86 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
  6.00 kJ/m²
@Temperature -40.0 °C		 2.86 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  50.0 kJ/m² 23.8 ft-lb/in² ISO 180/1U
  30.0 kJ/m²
@Temperature -40.0 °C		 14.3 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1U
  50.0 kJ/m²
@Temperature -30.0 °C		 23.8 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1U
Charpy Impact Unnotched  4.50 J/cm² 21.4 ft-lb/in² ISO 179/1eU
  4.00 J/cm²
@Temperature -40.0 °C		 19.0 ft-lb/in²
@Temperature -40.0 °F		 ISO 179/1eU
  4.50 J/cm²
@Temperature -30.0 °C		 21.4 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.700 J/cm² 3.33 ft-lb/in² ISO 179/1eA
  0.700 J/cm²
@Temperature -30.0 °C		 3.33 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
  0.700 J/cm²
@Temperature -40.0 °C		 3.33 ft-lb/in²
@Temperature -40.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour   2010 MPa
@Pressure 40.0 MPa,
Temperature 60.0 °C		 292000 psi
@Pressure 5800 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2160 MPa
@Pressure 35.0 MPa,
Temperature 60.0 °C		 313000 psi
@Pressure 5080 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2340 MPa
@Pressure 30.0 MPa,
Temperature 60.0 °C		 340000 psi
@Pressure 4350 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2540 MPa
@Pressure 25.0 MPa,
Temperature 60.0 °C		 369000 psi
@Pressure 3630 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2740 MPa
@Pressure 20.0 MPa,
Temperature 60.0 °C		 397000 psi
@Pressure 2900 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2910 MPa
@Pressure 15.0 MPa,
Temperature 60.0 °C		 422000 psi
@Pressure 2180 psi,
Temperature 140 °F		 ISO 11403-1 -2
  3030.3 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 439510 psi
@Pressure 1450 psi,
Temperature 140 °F		 ISO 11403-1 -2
  3110 MPa
@Pressure 5.00 MPa,
Temperature 60.0 °C		 451000 psi
@Pressure 725 psi,
Temperature 140 °F		 ISO 11403-1 -2
  5050.5 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 732510 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5330 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 774000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5450 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 791000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5560 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 806000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5637.5 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 817650 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5300 MPa
@Time 3600 sec		 769000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours   1370 MPa
@Pressure 40.0 MPa,
Temperature 60.0 °C		 199000 psi
@Pressure 5800 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1470 MPa
@Pressure 35.0 MPa,
Temperature 60.0 °C		 213000 psi
@Pressure 5080 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1587.3 MPa
@Pressure 30.0 MPa,
Temperature 60.0 °C		 230220 psi
@Pressure 4350 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1680 MPa
@Pressure 25.0 MPa,
Temperature 60.0 °C		 244000 psi
@Pressure 3630 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1750 MPa
@Pressure 20.0 MPa,
Temperature 60.0 °C		 254000 psi
@Pressure 2900 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1850 MPa
@Pressure 15.0 MPa,
Temperature 60.0 °C		 268000 psi
@Pressure 2180 psi,
Temperature 140 °F		 ISO 11403-1 -2
  1960 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 284000 psi
@Pressure 1450 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2050 MPa
@Pressure 5.00 MPa,
Temperature 60.0 °C		 297000 psi
@Pressure 725 psi,
Temperature 140 °F		 ISO 11403-1 -2
  3730 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 541000 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4000 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 580000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4140 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 601000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4170 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 604000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4350 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 631000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4300 MPa
@Time 3.60e+6 sec		 624000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+15 ohm 1.00e+15 ohm IEC 60093
Dielectric Constant   3.5
@Frequency 1.00e+6 Hz		 3.5
@Frequency 1.00e+6 Hz		 IEC 60250
  4.1
@Frequency 100 Hz		 4.1
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  27.0 kV/mm 686 kV/in IEC 60243-1
Dissipation Factor   0.0020
@Frequency 100 Hz		 0.0020
@Frequency 100 Hz		 IEC 60250
  0.0080
@Frequency 1000 Hz		 0.0080
@Frequency 1000 Hz		 ASTM D150
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 IEC 60250
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 ASTM D150
Comparative Tracking Index  350 V 350 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  50.0 µm/m-°C 27.8 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  1.90 J/g-°C 0.454 BTU/lb-°F  
Thermal Conductivity  0.240 W/m-K 1.67 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  220 °C 428 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  200 °C 392 °F ISO 75-1/-2
Vicat Softening Point  205 °C 401 °F 50°C/h 50N; ISO 306
Glass Transition Temp, Tg  55.0 °C 131 °F 10°C/min; ISO 11357-1/-2
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Flame Spread  30 mm/min
@Thickness 1.00 mm		 1.2 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
Oxygen Index  19 % 19 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT-GF15< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT-GF15  
UL recognition UL


上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40914.html

免责声明: 本文 杜邦高性能聚合物sk602 NC010/20%的玻璃纤维填充 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4