杜邦高性能聚合物sk643fr NC010/20%的玻纤填充

杜邦高性能聚合物Crastin®sk643fr NC010聚对苯二甲酸丁二醇酯（PBT） 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT）；聚对苯二甲酸丁二醇酯（PBT），20%的玻璃纤维填充 材料说明：20%玻纤增强阻燃聚对苯二甲酸丁二醇酯 Crastin sk643fr是阻燃玻璃纤维增强聚对苯二甲酸乙二醇酯成型树脂20%。这是公认的UL94V-0在0.8mm。
 物性表：

 
Physical Properties Metric English Comments
Density  1.63 g/cc 0.0589 lb/in³ ISO 1183
Water Absorption  0.32 %
@Thickness 2.00 mm		 0.32 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.130 %
@Thickness 2.00 mm		 0.130 %
@Thickness 0.0787 in		 Sim. to ISO 62
Linear Mold Shrinkage, Flow  0.0050 cm/cm 0.0050 in/in ISO 294-4 2577
  0.0060 cm/cm 0.0060 in/in annealed; ISO 294-4
Linear Mold Shrinkage, Transverse  0.012 cm/cm 0.012 in/in ISO 294-4 2577
  0.0145 cm/cm 0.0145 in/in annealed; ISO 294-4
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  113 MPa 16400 psi ISO 527-1/-2
Tensile Stress   6.14 MPa
@Strain 0.250 %,
Temperature 160 °C		 891 psi
@Strain 0.250 %,
Temperature 320 °F		 ISO 11403-1 -2
  16.1 MPa
@Strain 0.250 %,
Temperature 40.0 °C		 2340 psi
@Strain 0.250 %,
Temperature 104 °F		 ISO 11403-1 -2
  20.0 MPa
@Strain 0.250 %,
Temperature 23.0 °C		 2900 psi
@Strain 0.250 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  23.5 MPa
@Strain 0.250 %,
Temperature 0.000 °C		 3410 psi
@Strain 0.250 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  24.8 MPa
@Strain 0.250 %,
Temperature -20.0 °C		 3600 psi
@Strain 0.250 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  25.5 MPa
@Strain 0.250 %,
Temperature -40.0 °C		 3700 psi
@Strain 0.250 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  26.3 MPa
@Strain 1.50 %,
Temperature 160 °C		 3810 psi
@Strain 1.50 %,
Temperature 320 °F		 ISO 11403-1 -2
  37.3 MPa
@Strain 3.00 %,
Temperature 160 °C		 5410 psi
@Strain 3.00 %,
Temperature 320 °F		 ISO 11403-1 -2
  77.7 MPa
@Strain 1.50 %,
Temperature 40.0 °C		 11300 psi
@Strain 1.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  86.8 MPa
@Strain 1.50 %,
Temperature 23.0 °C		 12600 psi
@Strain 1.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  104 MPa
@Strain 1.50 %,
Temperature 0.000 °C		 15100 psi
@Strain 1.50 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  108 MPa
@Strain 1.50 %,
Temperature -20.0 °C		 15700 psi
@Strain 1.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  111 MPa
@Strain 1.50 %,
Temperature -40.0 °C		 16100 psi
@Strain 1.50 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Elongation at Break  3.0 % 3.0 % ISO 527-1/-2
Tensile Modulus  8.50 GPa 1230 ksi ISO 527-1/-2
Flexural Strength  170 MPa 24700 psi ISO 178
Secant Modulus   1.62 GPa
@Strain 3.50 %,
Temperature 100 °C		 235 ksi
@Strain 3.50 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.81 GPa
@Strain 3.50 %,
Temperature 80.0 °C		 263 ksi
@Strain 3.50 %,
Temperature 176 °F		 ISO 11403-1 -2
  2.84 GPa
@Strain 1.50 %,
Temperature 100 °C		 412 ksi
@Strain 1.50 %,
Temperature 212 °F		 ISO 11403-1 -2
  3.03 GPa
@Strain 1.50 %,
Temperature 80.0 °C		 439 ksi
@Strain 1.50 %,
Temperature 176 °F		 ISO 11403-1 -2
  3.94 GPa
@Strain 0.250 %,
Temperature 100 °C		 571 ksi
@Strain 0.250 %,
Temperature 212 °F		 ISO 11403-1 -2
  4.24 GPa
@Strain 0.250 %,
Temperature 80.0 °C		 615 ksi
@Strain 0.250 %,
Temperature 176 °F		 ISO 11403-1 -2
  5.18 GPa
@Strain 1.50 %,
Temperature 40.0 °C		 751 ksi
@Strain 1.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  5.79 GPa
@Strain 1.50 %,
Temperature 23.0 °C		 839 ksi
@Strain 1.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  6.44 GPa
@Strain 0.250 %,
Temperature 40.0 °C		 934 ksi
@Strain 0.250 %,
Temperature 104 °F		 ISO 11403-1 -2
  6.93 GPa
@Strain 1.50 %,
Temperature 0.000 °C		 1010 ksi
@Strain 1.50 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  7.20 GPa
@Strain 1.50 %,
Temperature -20.0 °C		 1040 ksi
@Strain 1.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  7.40 GPa
@Strain 1.50 %,
Temperature -40.0 °C		 1070 ksi
@Strain 1.50 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  8.00 GPa
@Strain 0.250 %,
Temperature 23.0 °C		 1160 ksi
@Strain 0.250 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  9.40 GPa
@Strain 0.250 %,
Temperature 0.000 °C		 1360 ksi
@Strain 0.250 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  9.92 GPa
@Strain 0.250 %,
Temperature -20.0 °C		 1440 ksi
@Strain 0.250 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  10.2 GPa
@Strain 0.250 %,
Temperature -40.0 °C		 1480 ksi
@Strain 0.250 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  8.00 kJ/m² 3.81 ft-lb/in² ISO 180/1A
  7.00 kJ/m²
@Temperature -30.0 °C		 3.33 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  36.0 kJ/m² 17.1 ft-lb/in² ISO 180/1U
  35.0 kJ/m²
@Temperature -30.0 °C		 16.7 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1U
Charpy Impact Unnotched  5.50 J/cm² 26.2 ft-lb/in² ISO 179/1eU
  5.30 J/cm²
@Temperature -30.0 °C		 25.2 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.850 J/cm² 4.04 ft-lb/in² ISO 179/1eA
  0.780 J/cm²
@Temperature -30.0 °C		 3.71 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour  7200 MPa
@Time 3600 sec		 1.04e+6 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours  5500 MPa
@Time 3.60e+6 sec		 798000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+15 ohm 1.00e+15 ohm IEC 60093
Dielectric Constant   3.7
@Frequency 1.00e+6 Hz		 3.7
@Frequency 1.00e+6 Hz		 IEC 60250
  3.8
@Frequency 100 Hz		 3.8
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  28.0 kV/mm 711 kV/in IEC 60243-1
Dissipation Factor   0.0030
@Frequency 100 Hz		 0.0030
@Frequency 100 Hz		 IEC 60250
  0.016
@Frequency 1.00e+6 Hz		 0.016
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  250 V 250 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  40.0 µm/m-°C 22.2 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  100 µm/m-°C 55.6 µin/in-°F ISO 11359-1/-2
  100 µm/m-°C
@Temperature -40.0 °C		 55.6 µin/in-°F
@Temperature -40.0 °F		 ISO 11403-1 -2
  100 µm/m-°C
@Temperature 23.0 °C		 55.6 µin/in-°F
@Temperature 73.4 °F		 ISO 11403-1 -2
  100 µm/m-°C
@Temperature 55.0 °C		 55.6 µin/in-°F
@Temperature 131 °F		 ISO 11403-1 -2
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  220 °C 428 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  205 °C 401 °F ISO 75-1/-2
Flammability, UL94  V-0
@Thickness 1.50 mm		 V-0
@Thickness 0.0591 in		 IEC 60695-11-10
  V-0
@Thickness 0.800 mm		 V-0
@Thickness 0.0315 in		 IEC 60695-11-10
Oxygen Index  31 % 31 % ISO 4589-1/-2
 
Descriptive Properties
Delivery form Pellets  
Part Marking Code >PBT-GF20FR(17)< ISO 11469
Processing Injection Moulding  
Regional Availability Europe  
  Near East/Africa  
Resin Identification PBT-GF20FR(17)  
UL recognition UL

图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40931.html

免责声明: 本文 杜邦高性能聚合物sk643fr NC010/20%的玻纤填充 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络