| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0180 - 0.0200 cm/cm | 0.0180 - 0.0200 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 155 | 155 | ISO 2039-2 |
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 8.00 % | 8.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 3.20 GPa | 464 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 86.0 MPa | 12500 psi | ISO 178 |
| Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ISO 75-1, -2 |
| Flammability, UL94 | HB @Thickness 0.790 mm |
HB @Thickness 0.0311 in |
|
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 65.0 - 93.0 °C | 149 - 199 °F | cavity |
| 250 - 260 °C | 482 - 500 °F | hot runner | |
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |
| Middle Barrel Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |