| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0060 cm/cm | 0.0010 - 0.0060 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 92 | 92 | ISO 2039-2 | ||
| Tensile Strength at Break | 77.0 MPa | 11200 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 1.3 % | 1.3 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 7.20 GPa | 1040 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 109 MPa | 15800 psi | ISO 178 | ||
| Flexural Modulus | 6.44 GPa | 934 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 4.40 kJ/m² | 2.09 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 1.70 J/cm² | 8.09 ft-lb/in² | ISO 179/1eU | ||
| 1.50 J/cm² @Temperature 30.0 °C |
7.14 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179/1eA | ||
| 0.450 J/cm² @Temperature 30.0 °C |
2.14 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 5.00e+15 ohm | 5.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.3 @Frequency 100 Hz |
3.3 @Frequency 100 Hz |
IEC 60250 | ||
| 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Comparative Tracking Index | 275 V | 275 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 31.0 µm/m-°C | 17.2 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 61.0 µm/m-°C | 33.9 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 206 °C | 403 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | ISO 75-1, -2 | ||
| Glass Transition Temp, Tg | 55.0 °C | 131 °F | ISO 11357-1,-2,-3 | ||
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 255 °C | 464 - 491 °F | |||
| Die Temperature | 250 - 255 °C | 482 - 491 °F | |||
| Melt Temperature | 235 - 255 °C | 455 - 491 °F | |||
| 265 °C | 509 °F | ISO 294 | |||
| Mold Temperature | 80.0 °C | 176 °F | ISO 294 | ||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| De |
|||||
| Remarks | To avoid discoloration, process temperatures should be kept below 510°F and shear heating should be minimized | ||||