LCP D130M 材料说明：说明：流量非常高的LCP适合封装。30%研磨玻璃
LCP D130M 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 65 | 65 | ISO 2039-2 |
| Tensile Strength at Break | 92.0 MPa | 13300 psi | 5 mm/min; ISO 527-2/1A |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527-2/1A |
| Tensile Modulus | 9.50 GPa | 1380 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Strength | 124 MPa | 18000 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.9 @Frequency 1e+6 Hz |
3.9 @Frequency 1e+6 Hz |
IEC 60250 |
| 4.4 @Frequency 100 Hz |
4.4 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0132 @Frequency 100 Hz |
0.0132 @Frequency 100 Hz |
IEC 60250 |
| 0.022 @Frequency 1e+6 Hz |
0.022 @Frequency 1e+6 Hz |
IEC 60250 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 12.0 µm/m-°C @Temperature 20.0 °C |
6.67 µin/in-°F @Temperature 68.0 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 38.0 µm/m-°C @Temperature 20.0 °C |
21.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359-2 |
| Melting Point | 330 °C | 626 °F | ISO 11357-1,2,3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1, -2 |