| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | |
| Water Absorption | 0.00 % | 0.00 % | |
| Melt Flow | 50 g/10 min | 50 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | |
| Elongation at Break | 30 % | 30 % | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| Modulus of Elasticity | 2.20 GPa | 319 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| 20.0 J/cm² @Temperature -30.0 °C |
95.2 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Constant | 3.0 @Frequency 100 Hz |
3.0 @Frequency 100 Hz |
|
| 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | |
| Dissipation Factor | 0.0075 @Frequency 100 Hz |
0.0075 @Frequency 100 Hz |
|
| 0.025 @Frequency 1e+6 Hz |
0.025 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | |
| Vicat Softening Point | 175 °C | 347 °F | 50°C/hr/50 N |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|