PPS/LCP C0711A
材料：树脂债券两个基板（PPS和LCP）：优良的热稳定性和成型性，processability维。因此freqtis®是广泛用于表面安装的电子组件。此外，论文的特点适当的化合物有高频器件的低介电材料上的帐户损失在高频率地区。
模塑化合物的介电常数freqtis®允许控制通过一个恒定的高介电陶瓷复合
PPS/LCP C0711A 形式：粒子 PPS/LCP C0711A 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.02 g/cc | 0.0730 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Flexural Strength | 180 MPa | 26100 psi | Flexural Strain: 2.2%; ISO 178 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 7.0 @Frequency 1e+6 Hz |
7.0 @Frequency 1e+6 Hz |
Volumetric method |
| Dissipation Factor | 0.0020 @Frequency 3.00e+9 Hz |
0.0020 @Frequency 3.00e+9 Hz |
Perturbation method by cavity resonator |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 10.0 µm/m-°C @Temperature 20.0 °C |
5.56 µin/in-°F @Temperature 68.0 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 20.0 °C |
27.8 µin/in-°F @Temperature 68.0 °F |
ISO 11359-2 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|