| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 |
| Linear Mold Shrinkage | 0.005 cm/cm @Thickness 2.00 mm |
0.005 in/in @Thickness 0.0787 in |
sheet with film gate at rim, mold temperature 80°C |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | |
| Melt Flow | 41.08 g/10 min @Load 2.16 kg, Temperature 250 °C |
41.08 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527-1/2 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/2 |
| Tensile Modulus | 5.80 GPa | 841 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.650 J/cm² @Temperature -30.0 °C |
3.09 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.650 J/cm² @Temperature 23.0 °C |
3.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | K20/P50; IEC 60243-1 |
| Comparative Tracking Index | 175 V | 175 V | 100 drops value; IEC 60112 |
| 200 V | 200 V | Test Solution A CTI; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 213 °C | 415 °F | Method A, 10 N; ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
IEC 60695 |
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
IEC 60695 |
|