LB502-01
材质说明：描述
LP 502-01自然是一种高分子量，高密度聚乙烯共聚物，专为大型零件，成品要求优异的物理性能吹塑。该材料具有良好的加工性能和最终使用性能的平衡，如具有优良的耐环境应力开裂的影响。
LB502-01 性能表：| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ASTM D1505 |
| ESCR 100% Igepal® | 500 hour | 500 hour | Condition A; ASTM D1693 |
| Melt Index of Compound | 11 g/10 min @Load 2.16 kg, Temperature 190 °C |
11 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | ASTM D638 |
| Elongation at Break | 800 % | 800 % | 2"/min; ASTM D638 |
| Flexural Modulus | 1.14 GPa | 165 ksi | tangent; ASTM D790 |
| Izod Impact, Notched | 4.00 J/cm | 7.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
| Vicat Softening Point | 270 °C | 518 °F | ASTM D1525 |