| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage | 0.015 cm/cm @Thickness 2.00 mm |
0.015 in/in @Thickness 0.0787 in |
sheet with film gate at rim, mold temperature 80°C |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | |
| Melt Flow | 209.6 g/10 min @Load 2.16 kg, Temperature 250 °C |
209.6 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 80 | 80 | ISO 868 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ISO 527-1/-2 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-1/2 |
| Elongation at Yield | 7.0 % | 7.0 % | Outer fiber strain at maximum stress, 5 mm/min; ISO 178 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527-1/-2 |
| Flexural Strength | 70.0 MPa | 10200 psi | at 3.5% strain, 5 mm/min; ISO 178 |
| 90.0 MPa | 13100 psi | 5 mm/min; ISO 178 | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.250 J/cm² @Temperature -30.0 °C |
1.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 100 Hz |
3.3 @Frequency 100 Hz |
IEC 60250 |
| 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
IEC 60250 |
| 0.023 @Frequency 1e+6 Hz |
0.023 @Frequency 1e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 575 V | 575 V | 100 drops value; IEC 60112 |
| 600 V | 600 V | Test Solution A CTI; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
Longitudinal; ISO 11359, DIN 53752 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359, DIN 53752 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 |
| Vicat Softening Point | 190 °C | 374 °F | Method B, 50 N; ISO 306 |
| 220 °C | 428 °F | Method A, 10 N; ISO 306 | |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695 |
|