| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00300 cm/cm | 0.00300 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.00900 cm/cm | 0.00900 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.10 % | 2.10 % | ISO 527-1/-2 | ||
| Tensile Modulus | 10.2 GPa | 1480 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 | ||
| Flexural Modulus | 8.94 GPa | 1300 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 8.50 kJ/m² @Temperature -40.0 °C |
4.04 ft-lb/in² @Temperature -40.0 °F |
ISO 180/1A | ||
| 9.50 kJ/m² @Temperature 23.0 °C |
4.52 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature -40.0 °C |
16.7 ft-lb/in² @Temperature -40.0 °F |
ISO 180/1U | ||
| 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |||
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -40.0 °C |
21.4 ft-lb/in² @Temperature -40.0 °F |
ISO 179/1eU | ||
| 5.20 J/cm² @Temperature 23.0 °C |
24.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -40.0 °C |
3.81 ft-lb/in² @Temperature -40.0 °F |
ISO 179/1eA | ||
| 0.850 J/cm² @Temperature -30.0 °C |
4.04 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| 0.950 J/cm² @Temperature 23.0 °C |
4.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 244 °C | 471 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
IEC 60695-11-10 | |||
| Flame Spread | 38.0 mm/min @Thickness 1.00 mm |
1.50 in/min @Thickness 0.0394 in |
Burning rate; ISO 3795 (FMVSS 302) | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | >= 280 °C | >= 536 °F | |||
| 285 °C | 545 °F | Optimum | |||
| <= 300 °C | <= 572 °F | ||||
| Mold Temperature | >= 110 °C | >= 230 °F | |||
| 120 °C | 248 °F | Optimum | |||
| <= 130 °C | <= 266 °F | ||||
| Ejection Temperature | 170 °C | 338 °F | |||
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
|||
| Moisture Content | 0.0200 % | 0.0200 % | |||
| Hold Pressure | 80.0 MPa | 11600 psi | |||
| De |
|||||
| Back pressure | As low as possible | ||||
| Drying Recommended | yes | ||||
| Emission of organic compounds (µgC/g) | 16 | VDA 277 | |||
| Fogging (mg) | 0 | G-value (condensate); ISO 6452 | |||
| Hold pressure time | 4 s/mm | ||||
| Max. screw tangential speed (m/s) | 0.2 | ||||
| Odor Class | 3 | VDA 270 | |||
| Part Marking Code | >PET-GF30< | ISO 11469 | |||
| Processing | Injection Molding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PET-GF30 | ISO 1043 |
|||