沙比克pc/abs c3650,Cycoloy合金料,型号C3650

沙比克pc/abs c3650,联系人: 夏先生 手 机: 13501802636 QQ :206135696 邮 箱 :205730283@qq.com
沙比克pc/abs c3650 是一种最广泛使用的工业热塑性塑料。PC/ABS 提供最理想的性能PC优越的强度和耐热性能和ABS的灵活性。
特点:
 1、综合性能较好,冲击强度较高,化学稳定性,电性能良好.
images颗粒1图1)

 2、与372有机玻璃的熔接性良好,制成双色塑件,且可表面镀铬,喷漆处理.
0003.(图2)

  3、有高抗冲、高耐热、阻燃、增强、透明等级别。
imageske粒(图3)

4、流动性比HIPS差一点,比PMMA、PC等好,柔韧性好。
颗粒2(图4)

  5、用途:适于制作一般机械零件,减磨耐磨零件,传动零件和电讯零件.
images 粒子(图5)
 
  6、同PVC(聚氯乙烯)一样在屈折处会出现白化现象。
下载keli2(图6)

典型应用范围:
汽车内外饰:仪表板,饰柱,仪表前盖,格栅,内外饰件  2.商务设备机壳和内置部件:笔记本/台式电脑,复印机,打印机,绘图仪,显示器 3.电信,移动电话外壳,附件以及智能卡(SIM卡):  4.电器产品,电子产品外壳,电表罩和壳体,家用开关,插头和插座,电缆电线管道  5.家用电器,如洗衣机,吹风机,微波炉内外部件等。
 
 物性表:
Physical Properties Metric English Comments
Specific Gravity  1.20 g/cc 1.20 g/cc ASTM D792
Density  1.18 g/cc 0.0426 lb/in³ ISO 1183
Water Absorption at Saturation  0.60 % 0.60 % ASTM D570
Linear Mold Shrinkage, Flow  0.0040 - 0.0060 cm/cm
@Thickness 3.20 mm
0.0040 - 0.0060 in/in
@Thickness 0.126 in
SABIC Method
Melt Flow  8.5 g/10 min
@Load 5.00 kg,
Temperature 260 °C
8.5 g/10 min
@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound  8.0 g/10 min
@Load 5.00 kg,
Temperature 260 °C
8.0 g/10 min
@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
 
Mechanical Properties Metric English Comments
Hardness, Rockwell R  124 124 ISO 2039-2
Hardness, H358/30  113 MPa 16400 psi ISO 2039-1
Tensile Strength at Break  50.0 MPa 7250 psi 5 mm/min; ISO 527
  51.0 MPa 7400 psi Type I, 50 mm/min; ASTM D638
  55.0 MPa 7980 psi 50 mm/min; ISO 527
Tensile Strength, Yield  55.0 MPa 7980 psi 5 mm/min; ISO 527
  64.0 MPa 9280 psi Type I, 50 mm/min; ASTM D638
  65.0 MPa 9430 psi 50 mm/min; ISO 527
Elongation at Break  35 % 35 % Type I, 50 mm/min; ASTM D638
  >= 50 % >= 50 % 50 mm/min; ISO 527
  55 % 55 % 5 mm/min; ISO 527
Elongation at Yield  3.0 % 3.0 % 5 mm/min; ISO 527
  4.5 % 4.5 % 50 mm/min; ISO 527
  4.9 % 4.9 % Type I, 50 mm/min; ASTM D638
Tensile Modulus  2.60 GPa 377 ksi 1 mm/min; ISO 527
  2.86 GPa 415 ksi 50 mm/min; ASTM D638
Flexural Yield Strength  100 MPa 14500 psi 2 mm/min; ISO 178
  101 MPa 14600 psi 1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus  2.68 GPa 389 ksi 1.3 mm/min, 50 mm span; ASTM D790
  2.70 GPa 392 ksi 2 mm/min; ISO 178
Izod Impact, Notched  6.94 J/cm 13.0 ft-lb/in ASTM D256
Izod Impact, Notched (ISO)  45.0 kJ/m² 21.4 ft-lb/in² 80*10*4; ISO 180/1A
   13.0 kJ/m²
@Temperature -30.0 °C
6.19 ft-lb/in²
@Temperature -22.0 °F
80*10*4; ISO 180/1A
  15.0 kJ/m²
@Temperature 0.000 °C
7.14 ft-lb/in²
@Temperature 32.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched  4.80 J/cm² 22.8 ft-lb/in² Edgew 80*10*4 sp=62mm; ISO 179/1eA
   1.30 J/cm²
@Temperature -30.0 °C
6.19 ft-lb/in²
@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy  64.0 J
@Temperature 23.0 °C
47.2 ft-lb
@Temperature 73.4 °F
ASTM D3763
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  >= 1.00e+15 ohm >= 1.00e+15 ohm ROA; IEC 60093
Dielectric Constant    2.7
@Frequency 1.00e+6 Hz
2.7
@Frequency 1.00e+6 Hz
IEC 60250
  2.8
@Frequency 50.0 - 60.0 Hz
2.8
@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength    17.0 kV/mm
@Thickness 3.20 mm
432 kV/in
@Thickness 0.126 in
in oil; IEC 60243-1
  25.0 kV/mm
@Thickness 1.60 mm
635 kV/in
@Thickness 0.0630 in
in oil; IEC 60243-1
  35.0 kV/mm
@Thickness 0.800 mm
889 kV/in
@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor    0.0040
@Frequency 50.0 - 60.0 Hz
0.0040
@Frequency 50.0 - 60.0 Hz
IEC 60250
  0.0060
@Frequency 1.00e+6 Hz
0.0060
@Frequency 1.00e+6 Hz
IEC 60250
  0.0060
@Frequency 50.0 - 60.0 Hz
0.0060
@Frequency 50.0 - 60.0 Hz
ASTM D150
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow    72.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
  80.0 µm/m-°C
@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F
@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow    72.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
  80.0 µm/m-°C
@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F
@Temperature 73.4 - 140 °F
ISO 11359-2
Thermal Conductivity  0.200 W/m-K 1.39 BTU-in/hr-ft²-°F ISO 8302
Deflection Temperature at 0.46 MPa (66 psi)  102 °C 216 °F Edgew 120*10*4 sp=100mm; ISO 75/Be
  100 °C
@Thickness 3.20 mm
212 °F
@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)  91.0 °C 196 °F Edgew 120*10*4 sp=100mm; ISO 75/Ae
  88.0 °C
@Thickness 3.20 mm
190 °F
@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point  108 °C 226 °F Rate B/50; ISO 306
  110 °C 230 °F Rate B/120; ISO 306
  110 °C 230 °F Rate B/50; ASTM D1525
UL RTI, Electrical  60.0 °C 140 °F UL 746B
UL RTI, Mechanical with Impact  60.0 °C 140 °F UL 746B
UL RTI, Mechanical without Impact  60.0 °C 140 °F UL 746B
Flammability, UL94    V-0
@Thickness 1.49 mm
V-0
@Thickness 0.0587 in
UL 94
  5VB
@Thickness 2.48 mm
5VB
@Thickness 0.0976 in
UL 94
Oxygen Index  37 % 37 % ISO 4589
 

供应原料,品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询:
联系人: 夏先生  
手  机:13501802636 
QQ    :205730283  
邮 箱 :205730283@qq.com 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41478.html

免责声明: 本文 沙比克pc/abs c3650,Cycoloy合金料,型号C3650 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4