| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | |
| Water Absorption | 0.00 % | 0.00 % | |
| Melt Flow | 13 g/10 min | 13 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | |
| Elongation at Break | 50 % | 50 % | |
| Elongation at Yield | 1.0 % | 1.0 % | |
| Modulus of Elasticity | 2.10 GPa | 305 ksi | |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | |
| 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.0 @Frequency 100 Hz |
2.0 @Frequency 100 Hz |
|
| 2.0 @Frequency 1e+6 Hz |
2.0 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 60.0 kV/mm | 1520 kV/in | |
| Dissipation Factor | 0.00030 @Frequency 100 Hz |
0.00030 @Frequency 100 Hz |
|
| 0.00030 @Frequency 1e+6 Hz |
0.00030 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 400 V | 400 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 °C | 178 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C | 163 °F | |
| Vicat Softening Point | 83.0 °C | 181 °F | 50°C/hr/50 N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Oxygen Index | 18 % | 18 % | |
.