A.舒尔曼 520聚碳酸酯/苯乙烯合金,优良的韧性和耐冲击

A.舒尔曼 520聚碳酸酯/苯乙烯合金 类别:聚合物;热塑性的;聚碳酸酯(PC);聚碳酸酯/苯乙烯合金;聚苯乙烯(PS) 优良的韧性和耐冲击的特点
物性表:
  
 
Physical Properties Metric English Comments
Density  1.13 g/cc 0.0408 lb/in³  
Linear Mold Shrinkage  0.0040 cm/cm 0.0040 in/in ASTM D955
 
Mechanical Properties Metric English Comments
Hardness, Rockwell R  110 110 ASTM D785
Tensile Strength, Ultimate  62.0 MPa 8990 psi ASTM D638
Elongation at Break  80 % 80 % ASTM D638
Flexural Strength  97.0 MPa 14100 psi ASTM D790
Flexural Modulus  2.80 GPa 406 ksi ASTM D790
Izod Impact, Notched  5.87 J/cm 11.0 ft-lb/in ASTM D256
Izod Impact, Unnotched  NB NB ASTM D256
 
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi)  129 °C 264 °F ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)  110 °C 230 °F ASTM D648
Glass Transition Temp, Tg  145 - 150 °C 293 - 302 °F  
 
Processing Properties Metric English Comments
Middle Barrel Temperature  246 - 277 °C 475 - 531 °F
 

图:

上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41544.html

免责声明: 本文 A.舒尔曼 520聚碳酸酯/苯乙烯合金,优良的韧性和耐冲击 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4