PK 95,TG-X,DCTP1120,DT11,ASX9 物性表: PK 95,TG-X,DCTP1120,DT11,ASX9物性表及特性介绍,PK 95,TG-X,DCTP1120,DT11,ASX9注塑参数详情,如需PK 95,TG-X,DCTP1120,DT11,ASX9下载, 可到相关下载区下载
品名(产品大类): Silicone
阻燃等级(Flame Class): b2
热丝着火性(HWI): e
高电流电弧着火性 (HAI): b
比较导电径迹(CTI): b
电气强度(RTI Elec): t
机械冲击(RTI Imp): t
机械强度(RTI Str): t
ul证书编号: E256821
UL厂家: SHIU LI TECHNOLOGY CO LTD
中国塑胶原料之家 http://www.su-jiao.com/ul/
E256821
SHIU LI TECHNOLOGY CO LTD
435 YONGFENG RD, BADE, TAOYUAN HSIEN 334 TW
PK 95, TG-X, DCTP1120, DT11, ASX9
Silicone Molding Resin (SIR), furnished as sheets
Min Thk Flame RTI RTI RTI Color (mm) Class HWI HAI Elec Imp Str GY 1.0 V-0 3 0 150 150 150 3.0 V-0 1 0 150 150 150
Comparative Tracking Index (CTI): 0 Inclined Plane Tracking (IPT): - Dielectric Strength (kV/mm): - Volume Resistivity (10x ohm-cm) : - High-Voltage Arc Tracking Rate (HVTR): 0 High Volt, Low Current Arc Resis (D495): 0 Dimensional Stability (%): -
ANSI/UL 94 small-scale test data does not pertain to building materials, furnishings and related contents. ANSI/UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components and parts of end-product devices and appliances, where the acceptability of the combination is determined by UL.
Report Date:
2010-04-15
Last Revised:
2011-05-31
联系人:赵经理
Thickness Test Name Test Method Units Tested (mm) Value Flammability IEC 60695-11-10 Class (color) 1.0 V-0 (GY) 3.0 V-0 (GY) Glow-Wire Flammability (GWFI) IEC 60695-2-12 C - - Glow-Wire Ignition (GWIT) IEC 60695-2-13 C - - IEC Comparative Tracking Index IEC 60112 Volts (Max) - - IEC Ball Pressure IEC 60695-10-2 C - - ISO Heat Deflection (1.80 MPa) ISO 75-2 C - - ISO Tensile Strength ISO 527-2 MPa - - ISO Flexural Strength ISO 178 MPa - - ISO Tensile Impact ISO 8256 kJ/m2 - - ISO Izod Impact ISO 180 kJ/m2 - - ISO Charpy Impact ISO 179-2 kJ/m2 - -
转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/
本文链接: http://www.su-jiao.com/ul/show-61793.html
免责声明: 本文 PK 95,TG-X,DCTP1120,DT11,ASX9 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络