ZY9150,ZY9160,ZY9170,ZY850,ZY450,ZY4452,ZY950 ul证书编号:E358292
ZY9150,ZY9160,ZY9170,ZY850,ZY450,ZY4452,ZY950 物性表: ZY9150,ZY9160,ZY9170,ZY850,ZY450,ZY4452,ZY950物性表及特性介绍,ZY9150,ZY9160,ZY9170,ZY850,ZY450,ZY4452,ZY950注塑参数详情,如需ZY9150,ZY9160,ZY9170,ZY850,ZY450,ZY4452,ZY950下载, 可到相关下载区下载
品名(产品大类): Silicone
阻燃等级(Flame Class): a1
热丝着火性(HWI): a
高电流电弧着火性 (HAI): a
比较导电径迹(CTI): a
电气强度(RTI Elec): t
机械冲击(RTI Imp): t
机械强度(RTI Str): t
ul证书编号: E358292
UL厂家: DONGGUAN NEW-ORIENT TECHNOLOGY CO LTD
http://www.su-jiao.com/ul/ UL黄卡查询
E358292
DONGGUAN NEW-ORIENT TECHNOLOGY CO LTD
BEIMEN XIANG TIANXIN VILLAGE, HUANG JIANG TOWN, DONGGUANGUANGDONG523756 CN
ZY9150, ZY9160, ZY9170, ZY850, ZY450, ZY4452, ZY950
Silicone Molding Resin (SIR), furnished as paste
Min Thk Flame RTI RTI RTI Color (mm) Class HWI HAI Elec Imp Str NC 1.5 HB - - 150 150 150 3.0 HB - - 150 150 150
Comparative Tracking Index (CTI): - Inclined Plane Tracking (IPT): - Dielectric Strength (kV/mm): - Volume Resistivity (10x ohm-cm) : - High-Voltage Arc Tracking Rate (HVTR): - High Volt, Low Current Arc Resis (D495): - Dimensional Stability (%): -
ANSI/UL 94 small-scale test data does not pertain to building materials, furnishings and related contents. ANSI/UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components and parts of end-product devices and appliances, where the acceptability of the combination is determined by UL.
Report Date:
2012-11-14
Last Revised:
2012-11-14
联系人:赵经理
Thickness Test Name Test Method Units Tested (mm) Value Flammability IEC 60695-11-10 Class (color) 1.5 HB75 (NC) 3.0 HB40 (NC) Glow-Wire Flammability (GWFI) IEC 60695-2-12 C - - Glow-Wire Ignition (GWIT) IEC 60695-2-13 C - - IEC Comparative Tracking Index IEC 60112 Volts (Max) - - IEC Ball Pressure IEC 60695-10-2 C - - ISO Heat Deflection (1.80 MPa) ISO 75-2 C - - ISO Tensile Strength ISO 527-2 MPa - - ISO Flexural Strength ISO 178 MPa - - ISO Tensile Impact ISO 8256 kJ/m2 - - ISO Izod Impact ISO 180 kJ/m2 - - ISO Charpy Impact ISO 179-2 kJ/m2 - -