vailability
|
|
|||
Features
|
|
|||
Forms
|
|
Physical |
Nominal Value
|
Unit
|
Test Method
|
Specific Gravity
|
1.14
|
g/cm³
|
ASTM D792 |
Molding Shrinkage - Flow
|
1.3 to 1.6
|
%
|
ASTM D955 |
Water Absorption (24 hr)
|
1.2
|
%
|
ASTM D570 |
Hardness |
Nominal Value
|
Unit
|
Test Method
|
Rockwell Hardness
|
ASTM D785 | ||
M-Scale
|
86
|
|
|
R-Scale
|
121
|
|
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Strength (Yield)
|
91.0
|
MPa
|
ASTM D638 |
Tensile Elongation (Break)
|
12
|
%
|
ASTM D638 |
Flexural Modulus
|
3170
|
MPa
|
ASTM D790 |
Flexural Strength (Yield)
|
119
|
MPa
|
ASTM D790 |
Compressive Strength
|
102
|
MPa
|
ASTM D695 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Notched Izod Impact (23°C, 3.18 mm)
|
37
|
J/m
|
ASTM D256 |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Deflection Temperature Under Load
|
ASTM D648 | ||
0.45 MPa, Unannealed
|
196
|
°C
|
|
1.8 MPa, Unannealed
|
78.9
|
°C
|
|
Melting Temperature
|
254 to 266
|
°C
|
|
CLTE - Flow
|
0.000072
|
cm/cm/°C
|
ASTM D696 |
Thermal Conductivity
|
0.25
|
W/m/K
|
ASTM C177 |
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Volume Resistivity
|
3.9E+13
|
ohm·cm
|
ASTM D257 |
Dielectric Strength
|
18
|
kV/mm
|
ASTM D149 |