Physical | Dry | Conditioned |
Unit
|
Test Method
|
Density (23°C)
|
1.36
|
--
|
g/cm³
|
ISO 1183 |
Spiral Flow 3, 4
|
83.0
|
--
|
cm
|
Internal Method |
Molding Shrinkage
|
ISO 294-4 | |||
Across Flow
|
1.3
|
--
|
%
|
|
Flow
|
0.20
|
--
|
%
|
|
Water Absorption (Saturation, 23°C)
|
5.2 to 5.8
|
--
|
%
|
ISO 62 |
Humidity Absorption - 62% RH (70°C)
|
1.9 to 2.1
|
--
|
%
|
ISO 1110 |
Hardness | Dry | Conditioned |
Unit
|
Test Method
|
Ball Indentation Hardness (H 961/30)
|
240
|
--
|
MPa
|
ISO 2039-1 |
Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
Tensile Modulus
|
10000
|
7100
|
MPa
|
ISO 527-2/1 |
Tensile Stress (Break)
|
200
|
130
|
MPa
|
ISO 527-2/5 |
Tensile Strain (Break)
|
3.0
|
5.5
|
%
|
ISO 527-2/5 |
Flexural Modulus 5
|
8800
|
7200
|
MPa
|
ISO 178 |
Flexural Strength 5
|
285
|
220
|
MPa
|
ISO 178 |
Impact | Dry | Conditioned |
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
-30°C
|
11
|
--
|
kJ/m²
|
|
23°C
|
12
|
16
|
kJ/m²
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
-30°C
|
80
|
--
|
kJ/m²
|
|
23°C
|
85
|
95
|
kJ/m²
|
Thermal | Dry | Conditioned |
Unit
|
Test Method
|
Heat Deflection Temperature
|
||||
0.45 MPa, Unannealed
|
260
|
--
|
°C
|
ISO 75-2/B |
1.8 MPa, Unannealed
|
255
|
--
|
°C
|
ISO 75-2/A |
8.0 MPa, Unannealed
|
210
|
--
|
°C
|
ISO 75-2/C |
Melting Temperature 6
|
262
|
--
|
°C
|
DIN EN 11357-1 |
CLTE
|
ISO 11359-2 | |||
Flow: 23 to 80°C
|
0.000019
|
--
|
cm/cm/°C
|
|
Transverse: 23 to 80°C
|
0.000095
|
--
|
cm/cm/°C
|
Electrical | Dry | Conditioned |
Unit
|
Test Method
|
Surface Resistivity
|
1.0E+12
|
--
|
ohm
|
IEC 60093 |
Volume Resistivity
|
1.0E+13
|
--
|
ohm·cm
|
IEC 60093 |
Comparative Tracking Index (Solution A)
|
600
|
--
|
V
|
IEC 60112 |
Flammability | Dry | Conditioned |
Unit
|
Test Method
|
Burning Rate 7 (1.00 mm)
|
< 100
|
--
|
mm/min
|
FMVSS 302 |
Flame Rating (0.800 mm)
|
HB
|
--
|
|
UL 94 |
Glow Wire Flammability Index (1.60 mm)
|
650
|
--
|
°C
|
IEC 60695-2-12 |