Availability
|
|
Filler / Reinforcement
|
|
Features
|
|
Forms
|
|
Physical |
Nominal Value
|
Unit
|
Test Method
|
Density
|
1.57
|
g/cm³
|
ISO 1183 |
Molding Shrinkage - Flow
|
0.25
|
%
|
ISO 294-4 |
Water Absorption
|
ISO 62 | ||
Saturation, 23°C
|
3.2
|
%
|
|
Equilibrium, 23°C, 50% RH
|
1.0
|
%
|
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Modulus (23°C)
|
14000
|
MPa
|
ISO 527-2 |
Tensile Stress (Break, 23°C)
|
125
|
MPa
|
ISO 527-2 |
Tensile Strain (Break, 23°C)
|
1.5
|
%
|
ISO 527-2 |
Flexural Modulus (23°C)
|
13000
|
MPa
|
ISO 178 |
Flexural Strength (23°C)
|
145
|
MPa
|
ISO 178 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Charpy Notched Impact Strength (23°C)
|
5.0
|
kJ/m²
|
ISO 179 |
Charpy Unnotched Impact Strength (23°C)
|
24
|
kJ/m²
|
ISO 179 |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Heat Deflection Temperature
|
|||
0.45 MPa, Unannealed
|
250
|
°C
|
ISO 75-2/B |
1.8 MPa, Unannealed
|
245
|
°C
|
ISO 75-2/A |
CLTE - Flow (23°C)
|
0.000022
|
cm/cm/°C
|
ISO 11359-2 |
Thermal Conductivity
|
1.2
|
W/m/K
|
ISO 8302 |
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Surface Resistivity
|
1.0E+12
|
ohm
|
ASTM D257 |
Electric Strength (2.00 mm)
|
38
|
kV/mm
|
IEC 60243-1 |
Comparative Tracking Index
|
600
|
V
|
IEC 60112 |
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Flame Rating (1.60 mm)
|
HB
|
|
UL 94 |
Additional Information | |||
The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods.
The value listed as Coefficient of Linear Thermal Expansion, Flow ISO 11359-1-2, was tested in accordance with ISO 7991. |