Diamaloy GLY FXW749|ASA|Diamond Polymers物性表报告及物性特性介绍,Diamaloy GLY FXW749|ASA|Diamond Polymers注塑参数详情-塑料物性表查询网

加工/物理特性	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
熔体流动指数(Melt Flow Index)	9.2	g/10min	ASTM D 1238
温度(Temperature)	220	°C	-
负载(Load)	10	kg	-
模具收缩(Mold Shrinkage) (MD)	0.55	mm/mm	ASTM D 955
密度(Density) (73°F)	1110	kg/m³	ASTM D 792

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
熔体流动指数(熔体流动指数(Melt flow index)) (MFI)	8	g/10min	ISO 1133
MFI温度(MFI temperature)	220	°C	ISO 1133
MFI负载(MFI load)	10	kg	ISO 1133

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	3060	MPa	ISO 527-1/-2
抗拉强度(Tensile Strength)	2.7	MPa	ISO 527-1/-2
屈服应力(Yield stress)	52	MPa	ISO 527-1/-2
Stress at 50% strain	14	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	42	MPa	ISO 527-1/-2
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	5	kJ/m²	ISO 179/1eA
弯曲弹性模量(Flexural modulus) (23°C)	2790	MPa	ISO 178
悬臂梁式冲击切口 (23°C)	5	kJ/m²	ISO 180/1A
悬臂梁式冲击切口	2	kJ/m²	ISO 180/1A
温度(Temperature)	-30	°C	ISO 180/1A
ASTM数据(ASTM Data)
抗拉强度(Tensile Strength) at Yield	53.8	MPa	ASTM D 638
抗拉强度(Tensile Strength) at Break	44.8	MPa	ASTM D 638
屈服伸长率(Elongation at Yield)	2.9	%	ASTM D 638
断裂伸长率(Elongation at Break)	8.5	%	ASTM D 638
弯曲弹性模量(弯曲弹性模量(Flexural Modulus))	2923.37	MPa	ASTM D 790
抗弯强度(Flexural Strength)	84.8	MPa	ASTM D 790
悬臂梁式冲击切口 (1/8 in)	0.0534	kJ/m	ASTM D 256

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	82	°C	ISO 75-1/-2
Vicat softening temperature A	97	°C	ISO 306
ASTM数据(ASTM Data)
热膨胀系数(Coefficient of Thermal Expansion) (MD)	90	E-6/K	ASTM D 696
热膨胀系数(Coefficient of Thermal Expansion) (TD)	102	E-6/K	ASTM D 696
DTUL @ 264 psi	80.6	°C	ASTM D 648
Vicat 温度(Temperature)	95	°C	ASTM D 1525

CharacteristicsProcessingSheet ExtrusionSpecial CharacteristicsU.V. stabilized or stable to weatherFeaturesMelt StrengthRegional AvailabilityNorth AmericaDisclaimerCopyright M-Base .