PA 2200 Top Quality 1.0|PA12|EOS物性表报告及物性特性介绍,PA 2200 Top Quality 1.0|PA12|EOS注塑参数详情-塑料物性表查询网

0 | PA12 |EOS Product TextsThis whitish fine powder PA 2200 on the basis of polyamide 12 serves with its very well-balanced property profile a wide variety of applications. Laser-sintered parts made from PA 2200 possess excellent material properties:g. metallisation, stove enamelling, vibratory grinding, tub colouring, bonding, powder coating, flocking) Due to the excellent mechanical properties the material is often used to substitute typical injection moulding plastics. The biocompatibility allows its use e.g. for prostheses, the high abrasion resistance allows e.g. the realisation of movable part connections. It applies a layer thickness of 60 µm, which is approximately the thickness of a grain of the plastic powder normally used today. The typical stair-step effect on upward and downward-pointing geometry elements can practically no longer be seen on TopQuality parts. The mechanical attributes of TopQuality parts are satisfyingly close to the levels of Performance parts.eos.info.

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	1800	MPa	ISO 527-1/-2
抗拉强度(Tensile Strength)	52	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	20	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	53	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	4.8	kJ/m²	ISO 179/1eA
弯曲弹性模量(Flexural modulus) (23°C)	1500	MPa	ISO 178
悬臂梁式冲击切口 (23°C)	4.4	kJ/m²	ISO 180/1A
Shore D hardness (15s)	75	-	ISO 868

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
熔化温度(熔化温度(Melting temperature)) (10°C/min)	176	°C	ISO 11357-1/-3
维卡软化温度（50℃/ h的50N）Vicat softening temperature	163	°C	ISO 306

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
密度(Density)	930	kg/m³	ISO 1183

CharacteristicsProcessingLaser SinteringDelivery formWhiteChemical ResistanceGeneral Chemical ResistanceEcological valuationUS Pharmacopeia Class VI ApprovedRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaDisclaimerCopyright M-Base .