Product TextsVESTAMID® L-CF15 blk1 / *	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	0.4 / *	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	8000 / 7500	MPa	ISO 527-1/-2
屈服应力(Yield stress)	* / 120	MPa	ISO 527-1/-2
屈服应变(Yield strain)	* / 6	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	* / 6.5	%	ISO 527-1/-2
破坏时应变(Stress at break)	120 / *	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	5 / *	%	ISO 527-1/-2
Tensile creep modulus (1h)	* / 5500	MPa	ISO 899-1
Tensile creep modulus (1000h)	* / 3900	MPa	ISO 899-1
简支梁冲击强度(Charpy impact strength) (+23°C)	60 / 65	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	70 / 70	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	14 / 20	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	13 / 12	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	178 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	170 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	175 / *	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	175 / *	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	1.75 / *	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	176 / *	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	3.2 / *	mm	IEC 60695-11-10

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
体积电阻率(Volume resistivity)	100 / *	Ohm*m	IEC 60093

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	1.3 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	0.5 / *	%	Sim. to ISO 62
密度(Density)	1080 / 1080	kg/m³	ISO 1183

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density) of melt	940	kg/m³	-
熔体热导率(Thermal conductivity of melt)	0.17	W/(m K)	-
规格的热容融化(Spec. heat capacity of melt)	2670	J/(kg K)	-

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	260	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	200	mm/s	ISO 294
Injection Molding, pressure at hold	70	MPa	ISO 294

Diagrams1 % The drying time is dependent on the drying temperature. At a drying temperature of 80°C we recommend, depending on the waterFresh air dryers are acceptable, better would be a dry air orPlease note our product literature, plasticized resins can lose plasticizer during drying. ISO 1817 Liquid C) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid 4) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid F) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid F) (90°C)[/td][/tr][tr][td] 4 Brake fluid (120°C)[/td][/tr][tr][td] .