VESTAMID® LX9102 blk (sw)|PA12|Evonik Industries物性表报告及物性特性介绍,VESTAMID® LX9102 blk (sw)|PA12|Evonik Industries注塑参数详情-塑料物性表查询网

Product TextsVESTAMID® LX9102 blk VESTAMID® LX9102 can be used e.g. in multilayer tubing MLT 140.2 and 2. Use of VESTAMID® LX9102 leads to 4 / *	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.5 / *	%	ISO 294-4, 2577

[tr][/tr][tr][/tr]

机械性能(机械性能(Mechanical properties))

dry / cond

单位(Unit)

测试标准(Test Standard)

ISO数据(ISO数据(CAMPUS/ISO) Data)

拉伸模量(Tensile Modulus)

640 / -

MPa

ISO 527-1/-2

屈服应力(Yield stress)

32 / -

MPa

ISO 527-1/-2

屈服应变(Yield strain)

37 / -

ISO 527-1/-2

断裂拉伸应变(Nominal strain at break)

>50 / -

ISO 527-1/-2

简支梁冲击强度(Charpy impact strength) (+23°C)

N / -

kJ/m²

ISO 179/1eU

简支梁冲击强度(Charpy impact strength) (-30°C)

N / -

kJ/m²

ISO 179/1eU

简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)

90[P] / -

kJ/m²

ISO 179/1eA

简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)

5 / -

kJ/m²

ISO 179/1eA

Partial Break

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	171 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	55 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	120 / *	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	136 / *	°C	ISO 306
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	3.2 / *	mm	IEC 60695-11-10

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
体积电阻率(Volume resistivity)	100 / -	Ohm*m	IEC 60093

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	1.5 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	0.5 / *	%	Sim. to ISO 62
密度(Density)	1120 / -	kg/m³	ISO 1183

CharacteristicsProcessingProfile ExtrusionDelivery formPelletsAdditivesPlasticizerSpecial CharacteristicsIncreased electrical conductivity, Anti-staticRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationProfile extrusionPREPROCESSING INFORMATION1 % The drying time is dependentAt a drying temperature of 80 °C we recommend, depending on the waterFresh air dryers are acceptable, better would be a dry air orPlease note our product literature, plasticized resins can lose plasticizer during ISO 1817 Liquid C) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid 4) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid F) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid F) (90°C)[/td][/tr][tr][td] 4 Brake fluid (120°C)[/td][/tr][tr][td] .