Xyron X0718|(PPE+PS)|Asahi Kasei物性表报告及物性特性介绍,Xyron X0718|(PPE+PS)|Asahi Kasei注塑参数详情-塑料物性表查询网

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
成型收缩(Molding shrinkage) (parallel)	0.6	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	0.8	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
抗拉强度(Tensile Strength)	44	MPa	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	35	%	ISO 527-1/-2
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	18	kJ/m²	ISO 179/1eA
弯曲弹性模量(Flexural modulus) (23°C)	2090	MPa	ISO 178
ASTM数据(ASTM Data)
抗拉强度(Tensile Strength)	44	MPa	ASTM D 638
断裂伸长率(Elongation at Break)	60	%	ASTM D 638
弯曲弹性模量(弯曲弹性模量(Flexural Modulus))	2090	MPa	ASTM D 790
抗弯强度(Flexural Strength)	65	MPa	ASTM D 790
悬臂梁式冲击切口 (1/4 in)	0.169	kJ/m	ASTM D 256

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	110	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	75	E-6/K	ISO 11359-1/-2
Burning behav. at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6	mm	IEC 60695-11-10
燃烧性厚度(Burning behav. at thickness h)	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	3.2	mm	IEC 60695-11-10
ASTM数据(ASTM Data)
UL 94 阻燃等级(Flame rating)	HB	-	UL 94
厚度测试(Thickness tested)	1.6	mm	-
热膨胀系数(Coefficient of Thermal Expansion) (MD)	75.1	E-6/K	ASTM D 696
DTUL @ 264 psi	115	°C	ASTM D 648

CharacteristicsApplicationsAutomotiveRegional AvailabilityNorth America, Europe, .