Polyethylene 158-14|(PE-LD)|UfaorgSyntez物性表报告及物性特性介绍,Polyethylene 158-14|(PE-LD)|UfaorgSyntez注塑参数详情-塑料物性表查询网

Polyethylene 158-14|(PE-LD)|UfaorgSyntez

Product TextsThe data for this material was provided by Plastinfo.ru.

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
熔体流动指数(熔体流动指数(Melt flow index)) (MFI)	2	g/10min	ISO 1133
MFI温度(MFI temperature)	190	°C	ISO 1133
MFI负载(MFI load)	2.16	kg	ISO 1133

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	280	MPa	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	>50	%	ISO 527-1/-2
破坏时应变(Stress at break)	11.3	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	>50	%	ISO 527-1/-2
弯曲弹性模量(Flexural modulus) (23°C)	98	MPa	ISO 178

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
熔化温度(熔化温度(Melting temperature)) (10°C/min)	110	°C	ISO 11357-1/-3
Vicat softening temperature A	100	°C	ISO 306

CharacteristicsProcessingInjection Molding, Film Extrusion, Profile Extrusion, Sheet Extrusion, Other Extrusion, Coating, Blow Molding, Transfer Molding, Thermoforming, Compression Molding, Rotational Molding, Blown Film Extrusion, Pipe/Tube Extrusion, Laser SinteringDelivery formBlackSpecial CharacteristicsLight stabilized or stable to light, U.V. stabilized or stable to weatherFeaturesDuctile, Heat Sealable, Non Blooming, HomopolymerChemical ResistanceAcid Resistance, Alkali Resistance, General Chemical Resistance, Solvent ResistanceApplicationsSlit FilmRegional AvailabilityEuropeDisclaimerCopyright M-Base .