EOS PEEK HP3|PEEK|EOS物性表报告及物性特性介绍,EOS PEEK HP3|PEEK|EOS注塑参数详情-塑料物性表查询网

Product TextsEOS provides the world-first high-performance polymer for the laser-sintering process - EOS PEEK HP3. Belonging to the group of Polyaryletherketone (PAEK), this semi-crystalline, thermoplastic material was developed for the use on the new high-temperature system EOSINT P 800. The laser-sintered parts achieve a tensile strength up to 95 MPa and a Young´s modulus up to 4400 MPa. These values are on an up to 100 percent higher level than the so far market dominating materials PA 12 and PA 11. The continuous use temperature ranges within 180 °C (mechanical dynamic), 240 °C (mechanical static) and 260 °C (electrical) depending on the field of application which could not be reached so far. EOS PEEK HP3 is characterized by an outstanding combination of properties likeg. in medicine, aerospace industry or motorsports. In medical applications the outstanding properties make this material an ideal replacement for stainless steel and titanium. And in aerospace and in motorsports where light weight and fire resistance are of largest importance, EOS PEEK HP3 has developed to an adequate metal replacement.eos.info.

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	4250	MPa	ISO 527-1/-2
抗拉强度(Tensile Strength)	90	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	2.8	%	ISO 527-1/-2

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
熔化温度(熔化温度(Melting temperature)) (10°C/min)	372	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	165	°C	ISO 75-1/-2

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
密度(Density)	1310	kg/m³	ISO 1183

CharacteristicsProcessingLaser SinteringSpecial CharacteristicsHeat stabilized or stable to heatChemical ResistanceGeneral Chemical Resistance, Hydrolytically StableRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America,.